Doping of polyaniline films with organic sulfonic acids in aqueous media and the effect of water on these doped films

Polyaniline (PANI) films in the form of emeraldine salt (ES) doped with aqueous organic sulfonic acids such as camphorsulfonic acid (CSA), p-toluenesulfonic acid (p-TSA) and dodecylbenzenesulfonic acid (DBSA) were studied. The ES films were obtained by treating the PANT in the form of emeraldine base (EB) with the aqueous solution of the acids. The dopant weight fraction (w), which is related to the mass gain during the redoping of EB, was in situ determined using a quartz crystal microbalance (QCM). The behaviour of PANT doping with different acids indicates that the uptake shows a slow diffusion process. The kinetics of the doping reaction is dominated by Fickian diffusion kinetics. The diffusion coefficients (D) of the dopant ions into the PANI chains were determined and were found to vary within the range of (1.6-18) x 10(-15) cm(2) s(-1). Moreover, the effect of water on these doped ES films was studied. The starting point is the fact that PANI-coated the electrode of QCM shows significant frequency shifts on exposure to water. The changes in the frequency as a function of treatment time in water were quantitatively measured. The response of the device suggests that the mass decrease under water exposure is due to dopant ions release. The latter films were dedoped by exposure to ammonia solution to obtain the EB film form. A further decrease in the mass of the films was observed. The percentage of the mass loss due to water exposure is found to be less than w determined during the dedoping process. (C) 2008 Elsevier Ltd. All rights reserved.