Ternary functionalised carbon nanofibers/polypyrrole/manganese oxide as high specific energy electrode for supercapacitor

A successful fabrication of ternary functionalised carbon nanofibers/polypyrrole/manganese oxide (f-CNFs/PPy/MnO2) composite was reported. The field emission scanning electron microscopy (FESEM) image had revealed a random distribution of granular PPy and spherical nanoparticles of MnO2 on the surface off-CNFs. The measured contact angle of f-CNFs indicated superhydrophilic nature which can enhance the surface wettability and ionic diffusion. The ternary f-CNR/PPy/MnO2 composite displayed a remarkable specific capacitance of 409.88 F/g compared with f-CNFs/MnO2 (322.96 F/g) and f-CNFs/PPy (290.83 F/g). The electrochemical properties of (CNFs/PPy/MnO2 had contributed to the appreciable specific energy of 42.53 Wh/kg at a specific power of 297.32 W/kg. The assembled f-CNFs/PPy/MnO2 composite also showed low resistance of charge transfer (R-ct) value (3.40 Omega) with a better cycle life (86.30% capacitance retention over 3000 cycles). Hence, ternary f-CNFs/PPy/MnO2 can be suggested as a high-performance electrode for supercapacitor.