Contact reactive brazing of Ti53311S alloy using Cu foil as interlayer: Interfacial microstructure and joining properties

被引：20
|
作者：
Song, X. G. [1 ,2 ]
Cao, J. [2 ]
Chen, H. Y. [2 ]
Wang, H. Q. [2 ]
Feng, J. C. [1 ,2 ]
机构：
[1] Harbin Inst Technol Weihai, Sch Mat Sci & Engn, Weihai 264209, Peoples R China
[2] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
来源：
MATERIALS & DESIGN | 2013年 / 46卷
基金：
中国国家自然科学基金;
关键词：
TITANIUM-ALLOY; STRENGTH PROPERTIES; FILLER-METAL; TI-6AL-4V; C103;
D O I：
10.1016/j.matdes.2012.11.044
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Contact reactive brazing of Ti53311S alloy was extensively evaluated using Cu foil as interlayer within the range of 940-1020 degrees C for 10 min. Effect of brazing temperature on the interfacial microstructure and its evolution as well as joining properties were investigated in detail. TiCu and Ti3Cu4 intermetallic compounds formed in joint by isothermal solidification and peritectic reaction (TiCu + L -> Ti3Cu4) when the brazing temperature was 940 degrees C. A eutectoid microstructure consisting of alpha-Ti and Ti2Cu phases was produced by the eutectoid reaction (beta-Ti -> alpha-Ti + Ti2Cu) in joint when brazed at 960-1000 degrees C. Whereas when brazing was conducted at 1020 degrees C (above the alpha -> beta transus temperature 1010 degrees C), Lamellar(alpha + beta) structure was obtained in joint by isothermal solidification and subsequent phase transformation. Tensile test indicated that the maximum average tensile strength reached 932.6 MPa at room temperature. Brittle fractures were observed in all of the brazed specimens although the fracture mode was different. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：895 / 901
页数：7
相关论文
共 50 条
  • [1] Interfacial Microstructure and Properties of Ti53311S Titanium Alloy Joints Brazed Using TiZrNiCu Filler Metal
    Song Xiaoguo
    Cao Jian
    Li Zhaoguang
    Zhang Zhiwei
    Feng Jicai
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 (08) : 1694 - 1698
  • [2] Interfacial microstructure and properties of Ti53311S titanium alloy joints brazed using TiZrNiCu filler metal
    Song, Xiaoguo
    Cao, Jian
    Li, Zhaoguang
    Zhang, Zhiwei
    Feng, Jicai
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2013, 42 (08): : 1694 - 1698
  • [3] Hot deformation microstructure and mechanism of Ti53311S titanium alloy
    Wang, Ruining
    Xi, Zhengping
    Zhao, Yongqing
    Qi, Yunlian
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2008, 37 (08): : 1356 - 1359
  • [4] Hot deformation microstructure and mechanism of Ti53311S titanium alloy
    Wang Ruining
    Xi Zhengping
    Zhao Yongqing
    Qi Yunlian
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (08) : 1356 - 1359
  • [5] Contact-reactive brazing of Ti3SiC2 ceramic to TC4 alloy using a Ni interlayer: Interfacial microstructure and joining properties
    Xia, Y. H.
    Wang, Y.
    Yang, Z. W.
    Wang, D. P.
    CERAMICS INTERNATIONAL, 2018, 44 (10) : 11869 - 11877
  • [6] Brazing high Nb containing TiAl alloy using Ti-28Ni eutectic brazing alloy: Interfacial microstructure and joining properties
    Si, X. Q.
    Zhao, H. Y.
    Cao, J.
    Song, X. G.
    Tang, D. Y.
    Feng, J. C.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 636 : 522 - 528
  • [7] Microstructure and properties of an Al–Ti–Cu–Si brazing alloy for SiC–metal joining
    Chun-duo Dai
    Rui-na Ma
    Wei Wang
    Xiao-ming Cao
    Yan Yu
    International Journal of Minerals,Metallurgy and Materials, 2017, 24 (05) : 557 - 565
  • [8] Microstructure and properties of an Al–Ti–Cu–Si brazing alloy for SiC–metal joining
    Chun-duo Dai
    Rui-na Ma
    Wei Wang
    Xiao-ming Cao
    Yan Yu
    International Journal of Minerals, Metallurgy, and Materials, 2017, 24 : 557 - 565
  • [9] Microstructure and properties of an Al-Ti-Cu-Si brazing alloy for SiC-metal joining
    Dai, Chun-duo
    Ma, Rui-na
    Wang, Wei
    Cao, Xiao-ming
    Yu, Yan
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2017, 24 (05) : 557 - 565
  • [10] Interfacial microstructure and joining properties of Titanium-Zirconium-Molybdenum alloy joints brazed using Ti-28Ni eutectic brazing alloy
    Song, X. G.
    Tian, X.
    Zhao, H. Y.
    Si, X. Q.
    Han, G. H.
    Feng, J. C.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 653 : 115 - 121
12345