Effect of ion irradiation of the metal matrix on the oxidation rate of Zircaloy-4

被引：13

作者：

Tupin, Marc ^{[1
]}

Verlet, Romain ^{[1
,4
]}

Colas, Kimberly ^{[1
]}

Jublot, Michael ^{[1
]}

Baldacchino, Gerard ^{[2
]}

Wolski, Krzysztof ^{[3
]}

机构：

[1] Univ Paris Sacaly, CEA Saclay, CEA DEN Serv Etud Mat Irradies, F-91191 Gif Sur Yvette, France

[2] Univ Paris Sacaly, CNRS, CEA, LIDYL, F-91191 Gif Sur Yvette, France

[3] Ecole Mines St Etienne, Ctr SMS, UMR5307, 158 Cours Fauriel, F-42023 St Etienne, France

[4] EDF, Ctr Renardieres, EDF R&D, F-77818 Ecuelles, Moret Sur Loing, France

来源：

CORROSION SCIENCE | 2018年 / 136卷

关键词：

Zircaloy-4; Oxidation; Irradiation; SIMS; Reactor conditions; TEMPERATURE PRESSURIZED-WATER; ZIRCONIUM ALLOYS; CORROSION KINETICS; IN-SITU; DAMAGE; MICROSTRUCTURE; ACCUMULATION; EVOLUTION; BEHAVIOR; REACTOR;

D O I：

10.1016/j.corsci.2018.02.023

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The oxidation kinetics acceleration observed in Zircaloy-4 cladding in Pressurized Water Reactor could be partially due to metal irradiation damage occuring in-pile. To check this assumption, several ion irradiation tests of the Zircaloy-4 metal matrix were performed to reproduce the evolution of the metallurgical state in reactor. This study showed that the amorphization process of the intermetallic precipitates (SPPs) does not change significantly the oxidation rate of Zircaloy-4. Implantation of iron in the matrix to simulate iron dissolution from the SPPs has no real impact on the corrosion kinetics. However proton irradiations at 350 degrees C producing < a > dislocation loops resulted in a significant increase in the oxidation rate.

引用

页码：28 / 37

页数：10

共 50 条

[1] Influence of light ion irradiation of the oxide layer on the oxidation rate of Zircaloy-4
Verlet, Romain
Tupin, Marc
Baldacchino, Gerard
Wolski, Krzysztof
Miro, Sandrine
Gosset, Dominique
Colas, Kimberly
Jublot, Michael
Jomard, Francois
CORROSION SCIENCE, 2015, 98 : 327 - 338
[2] Effect of ion irradiation on microstructure and hardness in Zircaloy-4
Zu, XT
Atzmon, M
Wang, LM
You, LP
Wan, FR
Was, GS
Adamson, RB
Effects of Radiation on Materials: 21st International Symposium, 2004, 1447 : 741 - 752
[3] Influence of light ion irradiation of the oxide layer on the oxidation rate of zircaloy-4: Irradiation of the post-transition oxide layer
Tupin, Marc
Venague, Boris
Gutierrez, Gaelle
CORROSION SCIENCE, 2019, 161
[4] Heavy ion irradiation induced defects in Zircaloy-4
Izerrouken, M.
Hazem, R.
Yahsi, U.
Naceri, S. E.
Tav, C.
Kuzeci, S.
Sari, A.
Haid, F.
Ishaq, A.
Menchi, O.
Ghamnia, M.
PHYSICA SCRIPTA, 2021, 96 (04)
[5] Effect of cerium ion implantation on the oxidation behavior of zircaloy-4 at 500 °C
Chen, XW
Bai, XD
Yu, HR
Zhou, QG
Chen, BS
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2002, 196 (3-4): : 293 - 298
[6] Corrosion resistance and microstructure of zircaloy-4 subjected to ion irradiation
Bai, XD
Chen, XW
Xu, J
Zhou, QG
Chen, BS
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2004, 217 (02): : 293 - 299
[7] MATRIX COMPOSITION OF ZIRCALOY-4
WADMAN, B
ROLANDER, U
ANDREN, HO
JOURNAL DE PHYSIQUE, 1987, 48 (C-6): : 299 - 304
[8] Observation of the effect of surface roughness on the oxidation of Zircaloy-4
Platt, P.
Allen, V.
Fenwick, M.
Gass, M.
Preuss, M.
CORROSION SCIENCE, 2015, 98 : 1 - 5
[9] Influence of Fe ion irradiation on the aqueous corrosion resistance of zircaloy-4
Chen, XW
Bai, XD
Peng, DQ
Zhou, QG
Chen, BS
JOURNAL OF MATERIALS SCIENCE LETTERS, 2003, 22 (21) : 1523 - 1526
[10] Formation and characterization of circular δ-hydride in Zircaloy-4 under ion irradiation
Li, Fusheng
Li, Shilei
Liu, Gang
Chen, Xudong
Wang, Yanli
JOURNAL OF NUCLEAR MATERIALS, 2019, 513 : 1 - 7

← 1 2 3 4 5 →