Synthesis and characterization of TiO2@C core-shell composite nanoparticles and evaluation of their photocatalytic activities

TiO2@C core-shell composite nanoparticles were synthesized by a simple and efficient single-step method in a specially made Swagelok cell at different temperatures. The prepared samples were characterized by XRD, diffuse reflectance-UV-vis, Raman, TEM, HRTEM, and N-2 adsorption-desorption methods. The carbon content in the samples can be varied with reaction time and temperature. It is evident from TEM analysis that the as-prepared samples are core-shell structures of TiO2, anatase phase, and C. The diameter of the TiO2@C nanoparticles is in the range of 15-35 nm. HRTEM results showed that a few graphitic layers were wrapped on the surface of TiO2, and these carbon layers are responsible for suppressing other phase formations of TiO2 even at high temperature. However, a few percentage points of the rutile phase are observed at high temperature (900 degrees C), evidenced from Raman analysis. The prepared samples were tested for their photochemical activities for 4-chlorophenol degradation. The sample prepared at 700 degrees C showed comparable activity for the degradation of 4-chlorophenol with that of Degussa P25. The photobleaching studies of methylene blue were also carried out under sunlight. It was found that the TiO2@C samples showed higher photocatalytic activity than Degussa P25.