Piezoelectric and Dielectric Properties of Acrylonitrile Butadiene Rubber/Lead Magnesio-Niobate Piezoelectric Ceram

A new composite with special piezoelectric property was prepared by using lead magnesio-niobate piezoelectric ceram powders (PMN) as dispersing phase in acrylonitrile butadiene rubber (NBR) matrix. The dielectric and piezoelectric properties of the composite were studied. The result shows that the particle size of 80% of PMN ceram powders was 0.5-2m. The piezoelectric constant (d33) of the composite increased with increasing volume fraction of PMN, and the max piezoelectric constant is 33 when the PMN volume fraction is 85%. Appropriate delay of polarizing time with increasing polarizing voltage could be helpful to improve the d33 value. The optional polarizing condition is 25min, 7-8kv/mm, and 80C. The dielectric constant increased with the increasing of the PMN volume fraction. Polarized time, polarized voltage, and polarized temperature have no effect on the dielectric constant.