Synthesis of monophase Al4O4C and the effect of Al4O4C addition to MgO-C refractory

被引:48
|
作者
Yu, Chao [1 ]
Zhu, Hongxi [1 ]
Yuan, Wenjie [1 ]
Deng, Chengji [1 ]
Cui, Peng [1 ]
Zhou, Shimin [1 ]
机构
[1] Wuhan Univ Sci & Technol, State Key Lab Breeding Base Refractories & Ceram, Wuhan 430081, Peoples R China
基金
中国国家自然科学基金;
关键词
Al4O4C; Synthesis; Aluminum content; Antioxidant; Oxidation; HEAT-TREATMENT; ALUMINUM; TEMPERATURE; POWDER; BRICKS; SIZE; AL;
D O I
10.1016/j.jallcom.2013.06.088
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Monophase Al4O4C ceramic powder was synthesized using a mixture of alpha-alumina, carbon black and aluminum powders as raw materials. The effects of different starting compositions and raw materials ratio on the phase transformation and micromorphology of Al4O4C were investigated. The results indicated that alpha-alumina, carbon black and aluminum powders was more appropriate as raw materials, and 20 mol% excess of aluminum resulted in single phase Al4O4C. Al2OC would occur if excessive carbon black was used. The Al content was found to have a significant effect on the microstructure of synthesized Al4O4C. Al4O4C added to the MgO-C refractory initially reacts with CO to form Al2O3 and C. After the reaction, the formed Al2O3 will further react with MgO to form MgAl2O4. The above reaction processes can form protective layers on the surfaces of the refractories, which inhibit the oxidation of the refractories. (c) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:348 / 354
页数:7
相关论文
共 50 条
  • [1] CRYSTALLOOPTICAL CONSTANTS OF AL4O4C
    CHISTYAKOV, AA
    GAVRISH, AM
    USTICHENKO, VA
    INORGANIC MATERIALS, 1991, 27 (08) : 1393 - 1395
  • [2] Effect of Na+ on the preparation of Al4SiC4/Al4O4C composite refractory
    State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China
    Rengong Jingti Xuebao, 4 (1127-1131):
  • [3] Synthesis and characterization of AlN whiskers by nitridation of Al4O4C
    Cheng, Keren
    Yu, Chao
    Ding, Jun
    Deng, Chengji
    Zhu, Hongxi
    Xue, Zhengliang
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 719 : 308 - 313
  • [4] Synthesis and characterisation of Al4O4C nanorod/CNT composites
    Yu, Chao
    Cheng, Keren
    Ding, Jun
    Deng, Chengji
    Xue, Zhengliang
    Wu, Xinxin
    Zhu, Hongxi
    CERAMICS INTERNATIONAL, 2017, 43 (14) : 11415 - 11420
  • [5] Chlorination-disproportionation of Al4O4C and Al4C3 in vacuum
    Feng, Yuebin
    Yang, Bin
    Yu, Qingchun
    Dai, Yongnian
    VACUUM, 2014, 109 : 206 - 211
  • [6] Influence of heating temperature, keeping time and raw materials grain size on Al4O4C synthesis in carbothermal reduction process and oxidation of Al4O4C
    Zhao, Jianli
    Lin, Wei
    Yamaguchi, Akira
    Ommyoji, Junji
    Sun, Halin
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2007, 115 (1346) : 654 - 660
  • [7] Decomposition of Al4O4C in the presence of C at high temperatures in vacuum
    Feng, Yuebin
    Hou, Hailan
    Yang, Bin
    Yang, Baomin
    Zi, Futing
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2018, 109 (05) : 399 - 404
  • [8] Effect of TiO2 on Synthesis of Al4SiC4/Al4O4C Composite
    DENG Chengji
    China's Refractories, 2010, 19 (02) : 19 - 24
  • [9] Al4O4C材料的高温氮化机理
    邢广超
    邓承继
    程可任
    丁军
    祝洪喜
    邸敬慧
    余超
    硅酸盐学报, 2021, 49 (12) : 2767 - 2775
  • [10] High-temperature Nitriding Mechanism of Al4O4C
    Xing G.
    Deng C.
    Cheng K.
    Ding J.
    Zhu H.
    Di J.
    Yu C.
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2021, 49 (12): : 2767 - 2775