Preparation of TiAl/Ti2AlC composites with Ti/Al/C powders by in-situ hot pressing

被引：0
|
作者：
Mei Bingchu [1 ]
Yan Ming [1 ]
Zhu Jiaoqun [1 ]
Zhou Weibing [1 ]
机构：
[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China
来源：
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2006年 / 21卷 / 02期
关键词：
Ti-Al-C system; TiAl / Ti2AlC composites; in-situ hot pressing; microstructure;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
TiAl/Ti2AlC composites were prepared by in-situ hot pressing of Ti/Al/C powders mixtures and siniered at different temperatures were investigated by X-ray diffraction (XRD) of samples. The reaction procedure of T-Al-C system could be divided into three stages. Below 900 degrees C, K reacts with Al to form TiAl intermetallies; above 900 V, C reacts with remain T to form KC triggered by the exothermal reaction of Ti and Al; TiAl reacts with TiC to produce dense TiAl/Ti-2 AlC composites. In the holding stage, ternary Ti-2 AlC develops to layered polycrystal and conposites pyknosis in the meanwhile. The mechanism of synthesis and microstructure was especially discussed.
引用
收藏
页码：14 / 16
页数：3
相关论文
共 50 条
  • [1] Preparation of TiAl/Ti2AlC Composites with Ti/Al/C powders by in-situ hot pressing
    Mei B.
    Yan M.
    Zhu J.
    Zhou W.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2006, 21 (2): : 14 - 16
  • [2] Preparation of TiAl/Ti2AlC Composites with Ti/Al/C Powders by In-situ Hot Pressing
    梅炳初
    严明
    JournalofWuhanUniversityofTechnology(MaterialsScienceEdition), 2006, (02) : 14 - 16
  • [3] Ti2AlC/TiAl Matrix Intermetallic Compound Prepared by In-situ Hot Pressing
    Ai, Taotao
    Wang, Fen
    Yang, Chenhui
    HIGH-PERFORMANCE CERAMICS VIII, 2014, 602-603 : 515 - 518
  • [4] Microstructure and mechanical properties of in situ TiAl/Ti2AlC composites prepared by reactive hot pressing
    Yang, Chen-hui
    Wang, Fen
    Ai, Tao-tao
    Zhu, Jian-feng
    CERAMICS INTERNATIONAL, 2014, 40 (06) : 8165 - 8171
  • [5] Preparation and properties of Ti2AlC/TiAl composites
    School of Materials Science and Engineering, Shaanxi University of Technology, Hanzhong, China
    Rengong Jingti Xuebao, (275-279):
  • [6] The phase transformation and microstructure of TiAl/Ti2AlC composites caused by hot pressing
    Chen Yan-Lin
    Yan Ming
    Sun Yi-Ming
    Mei Bing-Chu
    Zhu Jiao-Qun
    CERAMICS INTERNATIONAL, 2009, 35 (05) : 1807 - 1812
  • [7] Fabrication of TiAl/Ti2AlC composite by reaction hot pressing
    Zhu, Jianfeng
    Yang, Wenwen
    Gong, Yiping
    ADVANCES IN MECHANICAL ENGINEERING, PTS 1-3, 2011, 52-54 : 842 - 845
  • [8] Reaction Synthesis of TiAl/Ti2AlC In Situ Composites
    Zhu, Jianfeng
    Yang, Wenwen
    Gong, Yiping
    ECO-MATERIALS PROCESSING AND DESIGN XII, 2011, 695 : 137 - 140
  • [9] Low-temperature synthesis and characterization of Ti2AlC/TiAl in situ composites via a reaction Hot-Pressing Process in the Ti3AlC2-Ti-Al system
    Taotao Ai
    Ning Yu
    Xiaoming Feng
    Niansuo Xie
    Wenhu Li
    Pengju Xia
    Metals and Materials International, 2015, 21 : 179 - 184
  • [10] Low-Temperature Synthesis and Characterization of Ti2AlC/TiAl in situ Composites via a Reaction Hot-Pressing Process in the Ti3AlC2-Ti-Al System
    Ai, Taotao
    Yu, Ning
    Feng, Xiaoming
    Xie, Niansuo
    Li, Wenhu
    Xia, Pengju
    METALS AND MATERIALS INTERNATIONAL, 2015, 21 (01) : 179 - 184
12345