Processing characteristics of poly(ethylene terephthalate): hydrolytic and thermal degradation

The effects of poly(ethylene terephthalate) (PET) resin moisture content and temperature exposure have been investigated in terms of material changes resulting from the injection moulding process. Two resins with initial carboxyl contents of 10 mueq/g PET and 20 mueq/g PET have been analysed. Preforms processed at different resin moisture contents and processing temperatures of 280, 290 and 300degreesC were evaluated in terms of carboxyl end-group concentration using a titration method. Intrinsic viscosities of the performs were also measured by solution viscosity. Mathematical models describing the relationships of carboxyl end-group concentration and intrinsic viscosity to the processing conditions were generated from the experimental data. Carboxyl end-groups formed were compared for both resins and shown to be dependent on initial carboxyl content in the resin. Reducing the initial carboxyl content in the resin has been shown to increase its hydrolytic stability. The hydrolytic effect on the overall molecular weight drop was separated from the thermal/thermal-oxidative degradation and shown to be dependent on both the processing temperature and the resin moisture content. (C) 2002 Society of Chemical Industry.