In situ SEM studies of the low cycle fatigue behavior of DZ4 superalloy at elevated temperature: Effect of partial recrystallization

被引：46
|
作者：
Ma, Xianfeng [1 ,2 ]
Shi, Hui-Ji [1 ]
机构：
[1] Tsinghua Univ, Sch Aerosp, AML, Beijing 100084, Peoples R China
[2] Univ Michigan, Dept Mat Sci & Engn, Ann Arbor, MI 48109 USA
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2014年 / 61卷
基金：
中国国家自然科学基金;
关键词：
Directionally solidified superalloy; Recrystallization; Low cycle fatigue; Short fatigue crack; in situ SEM; DIRECTIONALLY SOLIDIFIED SUPERALLOY; SINGLE-CRYSTAL; ALLOY; CRACKS; GROWTH;
D O I：
10.1016/j.ijfatigue.2013.11.001
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The influence of partial recrystallization (RX) on the low cycle fatigue (LCF) behavior of directionally solidified DZ4 superalloy was studied using in situ scanning electron microscopy. Three typical recrystallization microstructures were prepared on the fatigue samples, via shot peening and subsequent heat treatment. The effect of RX on LCF life is evidently related to the specific RX microstructure. The RX layer does not necessarily reduce the LCF life. The fatigue crack initiation and short crack propagation behaviors for both raw DZ4 and recrystallized samples were in situ examined, which rationalized the observed effect of recrystallization on the LCF life variation. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：255 / 263
页数：9
相关论文
共 50 条
  • [1] Effect of surface recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ4 by in-situ SEM studies
    Ma, Xianfeng
    Shi, Hui-ji
    THERMEC 2011, PTS 1-4, 2012, 706-709 : 2456 - 2461
  • [2] Effect of recrystallization on low-cycle fatigue behavior of DZ4 directionally-solidified superalloy
    Tsinghua University, Beijing 100084, China
    Hangkong Cailiao Xuebao, 2006, 1 (71-75):
  • [3] Effect of recrystallization on low-cycle fatigue behavior of DZ4 directionally-solidified superalloy
    Shi, HJ
    Zhang, HF
    Wu, YQ
    FRACTURE AND STRENGTH OF SOLIDS VI, PTS 1 AND 2, 2006, 306-308 : 175 - 180
  • [4] On The Fatigue Short Crack Behaviors of Directionally Solidified Superalloy DZ4 by In Situ SEM Observations
    Ma, Xianfeng
    Shi, Huiji
    MATERIALS AND PRODUCT TECHNOLOGIES, 2010, 118-120 : 289 - 293
  • [5] On the fatigue small crack behaviors of directionally solidified superalloy DZ4 by in situ SEM observations
    Ma, Xianfeng
    Shi, Hui-Ji
    INTERNATIONAL JOURNAL OF FATIGUE, 2012, 35 (01) : 91 - 98
  • [6] Investigation on low cycle fatigue and fracture behaviors of directionally solidified DZ4 superalloy
    Zhang, WF
    Li, YJ
    Gao, W
    Fan, JJ
    Tao, CH
    RARE METAL MATERIALS AND ENGINEERING, 2005, 34 (02) : 217 - 220
  • [7] Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4
    Nie, Baohua
    Zhao, Zihua
    Liu, Shu
    Chen, Dongchu
    Ouyang, Yongzhong
    Hu, Zhudong
    Fan, Touwen
    Sun, Haibo
    MATERIALS, 2018, 11 (01):
  • [8] Influence of Torsional Pre-deformation on the Low Cycle Fatigue Life of Directionally Solidified Superalloy DZ4
    Zhang Weifang
    Liu Xiao
    Liu Shengwang
    Wang Zongren
    Li Yunju
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (09) : 1602 - 1606
  • [9] Effects of recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ40M
    Zhao Yang
    Wang Lei
    Li Hongyun
    Yu Teng
    Liu Yang
    RARE METALS, 2008, 27 (04) : 425 - 428
  • [10] Effects of recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ40M
    ZHAO Yang
    RareMetals, 2008, (04) : 425 - 428
12345