Improved growth of large YBCO single crystals

被引：13
|
作者：
Yao, X
Egami, M
Namikawa, Y
Mizukoshi, T
Shiohara, Y
Tanaka, S
机构：
[1] Super. Conduct. Research Laboratory, ISTEC, Tokyo 135
来源：
JOURNAL OF CRYSTAL GROWTH | 1996年 / 165卷 / 1-2期
关键词：
D O I：
10.1016/0022-0248(96)00206-0
中图分类号：
O7 [晶体学];
学科分类号：
0702 ; 070205 ; 0703 ; 080501 ;
摘要：
A new crystal pulling process was developed to produce large YBCO (Y123) single crystals under 1 atm oxygen pressure at a high growth rate, 1.5-2.5 times higher than that in air. A large crystal, 19.8 x 19.5 mm(2) in the a-b plane and 16.5 mm in thickness, was obtained. It is clear that a high oxygen partial pressure played a significant role in increasing the growth rate. The superconducting transition temperature T-c was measured to be 92.7 K for an oxygenated sample.
引用
收藏
页码：198 / 201
页数：4
相关论文
共 50 条
  • [1] GROWTH OF BSCCO AND YBCO SINGLE CRYSTALS USING LARGE TEMPERATURE GRADIENTS
    Yang, G.
    Sutton, S.
    Shang, P.
    Gough, C. E.
    Abell, J. S.
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1993, 3 (01) : 1663 - 1666
  • [2] DOUBLE CRUCIBLE METHOD FOR THE GROWTH OF LARGE SUPERCONDUCTING YBCO SINGLE-CRYSTALS
    WANG, YS
    BENNEMA, P
    VANDERLINDEN, P
    JOURNAL OF CRYSTAL GROWTH, 1990, 106 (2-3) : 483 - 486
  • [3] Improved growth technology of large MgO single crystals
    Zhang, Xu
    Xue, Dongfeng
    Wang, Jiyang
    Feng, Xiqi
    JOURNAL OF CRYSTAL GROWTH, 2006, 292 (02) : 505 - 509
  • [4] GROWTH AND CHARACTERIZATION OF YBCO SINGLE-CRYSTALS
    SURESHKUMAR, P
    SUBRAMANIAN, C
    RAMASAMY, P
    CRYSTAL RESEARCH AND TECHNOLOGY, 1989, 24 (11) : K207 - K211
  • [5] GROWTH AND MICROINDENTATION STUDIES OF YBCO SINGLE-CRYSTALS
    SURESHKUMAR, P
    SUBRAMANIAN, C
    RAMASAMY, P
    FERROELECTRICS, 1990, 102 : 347 - 350
  • [6] HOMOEPITAXIAL GROWTH OF YBCO THIN-FILMS ON YBCO SINGLE-CRYSTALS
    KONISHI, M
    WEN, JG
    FUKE, H
    MATSUNAGA, Y
    HAYASHI, K
    ODAGAWA, A
    ENOMOTO, Y
    SAKAI, H
    YAMADA, Y
    KOYAMA, S
    SHIOHARA, Y
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1995, 5 (02) : 1229 - 1232
  • [7] GROWTH AND PROPERTIES OF SUPERCONDUCTING YBCO SINGLE-CRYSTALS
    LIANG, RX
    DOSANJH, P
    BONN, DA
    BAAR, DJ
    CAROLAN, JF
    HARDY, WN
    PHYSICA C, 1992, 195 (1-2): : 51 - 58
  • [8] GROWTH OF LARGE AND UNTWINNED SINGLE-CRYSTAL OF YBCO
    LIN, CT
    ZHOU, W
    LIANG, WY
    SCHONHERR, E
    BENDER, H
    PHYSICA C, 1992, 195 (3-4): : 291 - 300
  • [9] THE GROWTH OF ZN-DOPED YBCO SINGLE-CRYSTALS
    LIN, CT
    LI, SX
    MACKENZIE, A
    ZHOU, W
    HUNNEYBALL, PD
    LIANG, WY
    PHYSICA C, 1992, 193 (1-2): : 129 - 136
  • [10] Growth of YBCO single crystals by the self-flux technique
    Liang, Ruixing
    Bonn, Douglas A.
    Hardy, Walter N.
    PHILOSOPHICAL MAGAZINE, 2012, 92 (19-21) : 2563 - 2581
12345