INFLUENCE OF HEAT TREATMENT ON MAGNETIC PROPERTIES OF NANOCRYSTALLINE Nd9Fe84Zr1B6 RIBBONS RECEIVED BY RAPID SOLIDIFICATION METHOD

被引：3
|
作者：
Ceglarek, A. [1 ]
Plusa, D. [1 ]
Pawlik, P. [1 ]
Dospial, M. [1 ]
机构：
[1] Czestochowa Tech Univ, Inst Phys, PL-42200 Czestochowa, Poland
来源：
ARCHIVES OF METALLURGY AND MATERIALS | 2012年 / 57卷 / 01期
关键词：
nanocomposites; rapid solidification method; Nd-Fe-B alloys; hard magnetic materials; nanocrystalline magnets;
D O I：
10.2478/v10172-012-0015-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The effect of the annealing on the phase composition and magnetic properties of nanocomposite melt-spun Nd9Fe84Zr1B6 ribbons has been investigated. From the X-ray diffraction studies confirmed be thermomagnetic curves measurements results that the microstructure of the material investigated is composed of a mixture of magnetically hard Nd2Fe14B and soft alpha-Fe, Fe3B nanosized grains. The small amount of undesirable Nd2Fe23B3 metastable phase has been found which do not decompose at the highest annealing temperature. The hysteresis loop measurements certify that the ribbon annealed at 863K show the best coupling between the hard and soft magnetic phases and thus the highest coercivity of 0.38T. The grain sizes increase with increasing annealing temperature causing the coercivity to be decrease.
引用
收藏
页码：229 / 232
页数：4
相关论文
共 50 条
  • [1] Influence of Mischmetal on the magnetic properties of B-rich Nd-Fe-B nanocrystalline ribbons
    Saccone, F. D.
    Sirkin, H.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2005, 294 (02) : E127 - E130
  • [2] INFLUENCE OF SOLIDIFICATION SPEED ON THE STRUCTURE AND MAGNETIC PROPERTIES OF Nd10Fe81Zr1B6 IN THE AS-CAST STATE
    Dospial, Marcin
    Nabialek, Marcin
    MATERIALI IN TEHNOLOGIJE, 2016, 50 (05): : 823 - 827
  • [3] Microstructure refinement and magnetic properties enhancement of nanocrystalline Nd12.3Fe81.7B6.0 ribbons by addition of Zr
    XiaoQian Bao
    Yi Qiao
    XueXu Gao
    Jie Zhu
    ShouZeng Zhou
    Science in China Series E: Technological Sciences, 2009, 52 : 1891 - 1896
  • [4] Microstructure refinement and magnetic properties enhancement of nanocrystalline Nd12.3Fe81.7B6.0 ribbons by addition of Zr
    Bao XiaoQian
    Qiao Yi
    Gao XueXu
    Zhu Jie
    Zhou ShouZeng
    SCIENCE IN CHINA SERIES E-TECHNOLOGICAL SCIENCES, 2009, 52 (07): : 1891 - 1896
  • [5] Influence of annealing on the magnetic properties and magneto-impedance response in Fe84Zr7B8Cu1 ribbons
    He, J
    Guo, HQ
    Shen, BG
    He, KY
    Zhang, HW
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 304 : 988 - 991
  • [6] Effect of Nd substitution on the soft magnetic properties of a nanocrystalline Fe84Nb7B9 alloy
    Takadate, K
    Kojima, A
    Makino, A
    Inoue, A
    SCRIPTA MATERIALIA, 2001, 44 (8-9) : 1401 - 1405
  • [7] Effects of nitrogen addition on the microstructures and soft magnetic properties of nanocrystalline Fe86Zr7B6Cu1 ribbons
    Tang, JC
    Du, YW
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2005, 293 (03) : 903 - 907
  • [8] Nects of hot isothermal pressing on the microstructures and soft magnetic properties of nanocrystalline Fe86Zr7B6Cu1 ribbons
    Tang, JC
    Wu, AH
    Mao, XY
    Li, SD
    Gao, WL
    Du, YW
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2004, 37 (02) : 151 - 154
  • [9] Effective Anisotropy Field Distribution of Soft Magnetic Nanocrystalline Fe84Zr3.5Nb3.5B8Cu1 Ribbons
    Modak, S. S.
    Mazaleyrat, F.
    Lo Bue, M.
    Varga, L. K.
    Kane, S. N.
    SOLID STATE PHYSICS, PTS 1 AND 2, 2012, 1447 : 1163 - +
  • [10] Effect of heat treatment on magnetic properties of nanocomposite Nd-lean Nd7Fe73B20 ribbons
    Caglar, Seyit
    Kilicaslan, M. Fatih
    Atasoy, Ahmet
    Tiryaki, Hasan
    Erkovan, Mustafa
    Hong, Soon-jik
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2021, 32 (02) : 2338 - 2345
12345