Investigation of Relationship Between Blend Ratio and Yarn Twist on Yarn Properties of Bamboo, Cotton, Polyester, and its Blends

In this study, a series of blended yarns consisting of 80:20 bamboo/cotton, 67:33 bamboo/cotton, 50:50 bamboo/cotton, 33:67 bamboo/cotton, 20:80 bamboo/cotton, 80:20 bamboo/polyester, 67:33 bamboo/polyester, 50:50 bamboo/polyester, 33:67 bamboo/polyester, and 20:80 bamboo/polyester were produced from blends consisting of bamboo/cotton and bamboo/ polyester. Besides these, 100% bamboo, 100% cotton, and 100% polyester were also produced. All the yarns were produced with two levels of twist per meter (TPM) 76 and 90. It can be found that the yarn unevenness characteristic was affected by the blended ratio of cotton, polyester, and regenerated bamboo fiber. The drop in tenacity of blended yarns in comparison to the constituents is generally lower which is attributed to the elongation at break of the yarns. The variability in tenacity in respect of 100% polyester yarn is quite high in comparison with other yarns. The yarn elongation at break of bamboo/cotton-blended yarns is found to be lower than those of bamboo/polyester-blended yarns. The variability in the work of rupture is found to be lower for bamboo/cotton- blended yarns. Yarn friction values of the yarns noticed that polyester exhibits the highest value at the TPM of 76. The yarn torque values from which it is noticed that 100% polyester yarns spun with the TPM of 76 have a higher torque in both the wet and dry states. The quality characters of yarn depend upon the ratio of bamboo, cotton, and polyester in the blend ratio.