Effect of Sr on microstructure and aging behavior of Mg-14Li alloys

The as-cast and as-extruded Mg-14 wt%Li-xSr (x=0.14, 0.19, 0.39 wt%) alloys were, respectively, prepared through a simple alloying process and hot extrusion. The effects of Sr addition on microstructure and aging behavior of the Mg-14 wt%Li-xSr alloys were studied. The results indicated that beta(Li) and Mg2Sr were the two primary phases in the microstructures of both as-cast and as-extruded Mg 14 wt%Li xSr alloys. Interestingly, with the increase of Sr content from 0.14 wt% to 0.39 wt%, the grain sizes of the as-cast and as-extruded Mg-14 wt%Li xSr alloys markedly decreased from 5000 mu m and 38 mu m to 330 mu m and 22 mu m respectively, while no obvious changes of the micro-hardness and microstructure of the as-extruded alloys were observed during the aging treatment. (C) 2012. Chinese Materials Research Society. Production and hosting by Elsevier Ltd. All rights reserved.