Low-temperature ordering of L10 FePt by PtMn underlayer

被引：49

作者：

Chiang, CC ^{[1
]}

Lai, CH ^{[1
]}

Wu, YC ^{[1
]}

机构：

[1] Natl Tsing Hua Univ, Dept Mat Sci & Engn, Hsinchu 300, Taiwan

来源：

APPLIED PHYSICS LETTERS | 2006年 / 88卷 / 15期

关键词：

D O I：

10.1063/1.2191422

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The ordering temperature of FePt films grown on PtMn underlayers was reduced due to phase transformation of the PtMn L1(0) phase. The in-plane coercivity of 10 nm FePt on 50 nm PtMn underlayers was 7688 Oe after annealing at 325 degrees C. An exchange field of 554 Oe was also observed, which indicates that PtMn may not only induce the ordering of FePt at a reduced temperature, but also may provide extra anisotropy. A large coercivity of 10500 Oe can be achieved for 35 nm FePt films on PtMn underlayers after 325 degrees C annealing.

引用

下载

页数：3

共 50 条

[1] Low-temperature ordering of L10 FePt phase in FePt thin film with AgCu underlayer
Yu, Y. S.
Li, Hai-Bo
Li, W. L.
Liu, Mei
Fei, W. D.
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2008, 320 (19) : L125 - L128
[2] The effect of GePt underlayer on L10 ordering FePt thin films
Hsu, C. J.
Tsai, J. L.
Hsu, C. W.
Chen, S. K.
Chang, W. C.
IEEE TRANSACTIONS ON MAGNETICS, 2006, 42 (10) : 2900 - 2902
[3] L10 CrPt underlayer thickness effects on FePt film ordering
Tsai, J. L.
Lin, Y. C.
Hsu, C. J.
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2008, 41 (02)
[4] The effect of Ag and Cu underlayer on the L10 ordering FePt thin films
Xu, XH
Wu, HS
Wang, F
Li, XL
APPLIED SURFACE SCIENCE, 2004, 233 (1-4) : 1 - 4
[5] Low-temperature ordering and enhanced coercivity of L10-FePt thin films with Al underlayer
Yang, F. J.
Wang, H.
Wang, H. B.
Wang, B. Y.
Wang, X. L.
Gu, H. S.
Yang, C. P.
APPLIED SURFACE SCIENCE, 2011, 257 (08) : 3216 - 3219
[6] Low-temperature ordering and enhanced coercivity of L10-FePt thin film promoted by a Bi underlayer
Feng, Chun
Li, Bao-He
Han, Gang
Teng, Jiao
Jiang, Yong
Liu, Quan-Lin
Yu, Guang-Hua
APPLIED PHYSICS LETTERS, 2006, 88 (23)
[7] Inductive magnetization of low-temperature ordered L 10 -FePt with CoAg underlayer
Lai, Yu-Cheng
Chang, Yen-Hwei
Chen, Yen-Chia
Liang, Chih-Hao
Chang, Wen-Cheng
Chiou, Chun-Mao
Chen, Guo-Ju
Journal of Applied Physics, 2007, 101 (05):
[8] Composition dependence of L10 ordering of FePt (001) thin films on MgO underlayer grown at room temperature
Zhang Li-Jiao
Cai Jian-Wang
ACTA PHYSICA SINICA, 2007, 56 (12) : 7266 - 7273
[9] Low-temperature ordering of FePt thin films by a thin AuCu underlayer
Zhu, Y
Cai, JW
APPLIED PHYSICS LETTERS, 2005, 87 (03)
[10] The L12 CrPt3 underlayer effect on the ordering of L10 FePt films
Tsai, J. L.
Lin, G. B.
Ou, C. L.
Chen, M. Y.
MATERIALS CHEMISTRY AND PHYSICS, 2010, 124 (01) : 380 - 384

← 1 2 3 4 5 →