On the α+γ⇆γ-phase boundary in nickel and in manganese containing stainless steel alloys

被引:0
|
作者
Schüle, W [1 ]
机构
[1] Univ Frankfurt, Inst Angew Phys, D-60325 Frankfurt, Germany
关键词
phase diagram; nickel and manganese containing stainless steels; nucleation; alpha-ferrite; alpha '-martensite; dislocations; volume change; brittleness;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The alpha -ferrite-phase in nickel and in manganese containing stainless steel alloys is very brittle. Its formation is connected with a huge decrease in volume, which also causes stresses in the alloys that are very dangerous if the materials cannot accommodate them. The alpha -ferrite-phase is formed in stainless steel alloys only if nucleation sites are provided. alpha ' -martensites are nucleation sites for the formation of alpha -ferrite, even at temperatures at which alpha -ferrite is not stable. If alpha ' -martensite is dissolved during an anneal, no new alpha -ferrite is formed, and the remaining alpha -ferrite transforms back into gamma -austenite. In "pure" nickel or in "pure" manganese containing stainless steel alloys the martensitic temperature is above 100 degreesC and thus alpha ' -martensite is always present at ambient temperature in these materials, giving rise to the formation of alpha -ferrite during a subsequent anneal. It was established in the present work that the gamma <----> gamma+alpha -phase boundary in iron-chromium-nickel alloys is also almost independent of the temperature as in iron-chromium-manganese alloys. Thus the existing phase diagram for nickel containing stainless steels has to be revised. The various elements added to "pure" stainless steel alloys, as we find them in EUR-316L, US-316L, US-PCA, and in AMCR, cause a drastic decrease of the martensitic temperature so that neither alpha ' -martensite nor alpha -ferrite is found in these alloys. However, in all these four alloys alpha -ferrite is formed readily during irradiation with high energy particles and a tentative gamma <----> gamma+alpha -phase boundary, valid during irradiation with high energy particles, is derived. The amount of alpha -ferrite formed during irradiation increases with decreasing irradiation temperature and with decreasing applied stress. The alloys EUR-316L, US-316L, US-PCA, and AMCR do not survive one reactor cycle, if irradiated at 100 degreesC.
引用
收藏
页码:704 / 721
页数:18
相关论文
共 50 条
  • [1] Irradiation creep in nickel containing and in manganese containing stainless steel alloys
    Hausen, H
    Schüle, W
    EFFECTS OF RADIATION ON MATERIALS: 18TH INTERNATIONAL SYMPOSIUM, 1999, 1325 : 742 - 764
  • [2] Materials of Construction: Stainless Steel Versus Nickel Alloys
    Signorelli, Rodrigo
    Li, Jan
    Chemical Engineering (United States), 2022, 129 (07): : 31 - 36
  • [3] STRIP CLADDING OF STEEL WITH STAINLESS AND NICKEL BASED ALLOYS
    HORSFIELD, AM
    ALMQVIST, G
    ROSENDAH.CH
    BRITISH WELDING JOURNAL, 1966, 13 (05): : 315 - +
  • [4] HOT-ROLLING OF CHROMIUM-NICKEL-MANGANESE STAINLESS-STEEL CONTAINING NITROGEN AND BORON
    KHOROSH, VA
    BULAT, SI
    MUKHINA, MA
    SOROKINA, NA
    YUSHCHENKO, KA
    STEEL IN THE USSR, 1976, 6 (12): : 677 - 678
  • [5] ORTHORHOMBIC DISTORTION IN GAMMA MANGANESE ALLOYS CONTAINING NICKEL
    HONDA, N
    TANJI, Y
    NAKAGAWA, Y
    JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 1975, 38 (02) : 589 - 589
  • [6] INVESTIGATION OF GRAIN BOUNDARY PHASE IN STAINLESS STEEL
    CLARK, CC
    MIHALISIN, JR
    CARROLL, KG
    TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1957, 209 : 1210 - 1211
  • [7] Smelting characteristics of nickel-chromium-manganese bearing prereduced pellets for the preparation of nickel saving austenite stainless steel master alloys
    Tian, Hongyu
    Chu, Mansheng
    Pan, Jian
    Zhu, Deqing
    Yang, Congcong
    Tang, Jue
    POWDER TECHNOLOGY, 2024, 441
  • [8] The pitting of stainless steel and nickel-based alloys in acetic acid solution containing bromine ion
    Liu, GQ
    Zhu, ZY
    Ke, W
    ACTA METALLURGICA SINICA, 2001, 37 (03) : 272 - 276
  • [9] SUPERPLASTICITY IN AN AUSTENITIC STAINLESS-STEEL CONTAINING ALUMINUM AND MANGANESE
    TOSCANO, EH
    SCRIPTA METALLURGICA, 1983, 17 (03): : 309 - 312
  • [10] Fume generation rates for stainless steel, nickel and aluminum alloys
    Castner, HR
    WELDING JOURNAL, 1996, 75 (12) : S393 - S401