Effect of HFMI treatment procedure on weld toe geometry and fatigue properties of high strength steel welds

The effects of high frequency mechanical impact (HFMI) treatment procedure on the weld toe geometry and fatigue strength in 1300 MPa yield strength steel welds were investigated. In this regard first the effect of three or six run treatments on the weld toe geometry was evaluated. The fatigue strength and weld toe geometry of as-welded and HFMI treated samples was then compared. Fatigue testing was done under fully reversed, constant amplitude bending load. When increasing the number of treatment runs from three to six, the weld toe radius and width of treatment remained almost constant. However, a slightly smaller depth of treatment in the base metal and a somewhat larger depth of treatment in the weld metal was observed. HFMI treatment increased the fatigue strength by 26%. The treatment did not increase the weld toe radius significantly, but resulted in a more uniform weld toe geometry along the weld. A depth of treatment in the base metal in the range of 0.15-0.19 mm and a width of treatment in the range of 2.5-3 mm, were achieved. It is concluded that the three run treatment would be a more economical option than the six run treatment providing a similar or even more favourable geometry modification. Copyright (C) 2016 The Authors. Published by Elsevier B.V.