Irradiation hardening of pure vanadium and vanadium alloys due to helium ion implantation and displacement damage

被引:12
|
作者
Yang, Yitao [1 ,2 ]
Yan, Tingxing [1 ,2 ]
Zhang, Chonghong [1 ,2 ]
Fu, Xin [3 ]
Ma, Tongda [3 ]
Niu, Mengke [1 ,2 ]
Ding, Zhaonan [1 ,2 ]
Gou, Jie [1 ,2 ]
Chen, Yuguang [1 ,2 ]
Song, Yin [1 ,2 ]
机构
[1] Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Peoples R China
[2] Univ Chinese Acad Sci, Sch Nucl Sci & Technol, Beijing 100049, Peoples R China
[3] Gen Res Inst Nonferrous Met, Natl Ctr Anal & Testing Nonferrous Met & Elect Ma, Beijing 100088, Peoples R China
基金
美国国家科学基金会;
关键词
Vanadium; Irradiation hardening; Nanoindentation; Helium; Dislocation loops; MECHANICAL-PROPERTIES; NEUTRON-IRRADIATION; TENSILE PROPERTIES; NANO-INDENTATION; LOW-TEMPERATURE; EVOLUTION; NANOINDENTATION; PRECIPITATION; BEHAVIOR; STEELS;
D O I
10.1016/j.jnucmat.2020.152381
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Pure V and V-5Cr-5Ti were irradiated by He and high-energy heavy ions to various doses. Nano-indentation was used to characterize the hardness change induced by ion irradiation. Under high-energy heavy ions irradiation, the hardness of pure V increased rapidly and saturated at very low damage level (0.03 dpa), the hardness of V-5Cr-5Ti increased slowly and tended to saturate at the damage higher than 0.4 dpa. In contrast to high-energy heavy-ion irradiation, more significant hardening occurred in both pure V and V-5Cr-5Ti under He ion irradiation. The significant hardening induced by He ion irradiation at the low dose was probably from the coarsening of dislocation loops due to the existence of He atoms in materials. TEM results revealed that He bubbles with high density have been formed in V-5Cr-5Ti at the high dose. The estimation based on the dispersion barrier hardening model suggested that He bubbles exhibited as weak obstacles due to the limitation of size, the major contribution to hardening was considered to be from dislocation loops. (C) 2020 Elsevier B.V. All rights reserved.
引用
收藏
页数:6
相关论文
共 50 条
  • [1] EFFECT OF IRRADIATION DAMAGE AND HELIUM ON SWELLING AND STRUCTURE OF VANADIUM-BASE ALLOYS
    CHUNG, HM
    LOOMIS, BA
    SMITH, DL
    JOURNAL OF NUCLEAR MATERIALS, 1994, 212 : 804 - 812
  • [2] Hydrogen and Neutron Irradiation Induced Hardening in Vanadium Alloys
    CHEN Jiming
    中国核科技报告, 2002, (00) : 943 - 948
  • [3] HELIUM-ION DAMAGE IN VANADIUM-2-PERCENT ZIRCONIUM ALLOYS
    PANDE, BM
    ANAND, MS
    AGARWALA, RP
    JOURNAL OF NUCLEAR MATERIALS, 1990, 171 (2-3) : 408 - 411
  • [4] IRRADIATION DAMAGE IN VANADIUM ALLOYS USING HEAVY-ION AND PROTON ACCELERATORS
    PHYTHIAN, WJ
    EYRE, BL
    BACON, DJ
    JOURNAL OF NUCLEAR MATERIALS, 1988, 155 (pt B) : 1274 - 1279
  • [5] Effect of cold work deformationon irradiation hardening of vanadium alloys
    Han, Xuxiao
    Niu, Mengke
    Yang, Yitao
    Zhang, Chonghong
    Meng, Xuan
    Li, Zengde
    Wang, Tieshan
    NUCLEAR FUSION, 2022, 62 (12)
  • [6] Helium retention of vanadium alloy after energetic helium ion irradiation
    Liu, X
    Yamada, T
    Yamauchi, Y
    Hirohata, Y
    Hino, T
    Noda, N
    FUSION ENGINEERING AND DESIGN, 2004, 70 (04) : 329 - 334
  • [7] Irradiation damage of helium-accumulated vanadium: atomic simulations
    Zhu, Xiaolu
    Wang, Canglong
    Hu, Nengwen
    Hu, Wangyu
    Duan, Wenshan
    Yang, Lei
    RSC ADVANCES, 2016, 6 (84): : 80939 - 80945
  • [8] Effects of helium on void swelling behavior of vanadium alloys using dual ion beam irradiation
    Iwai, T
    Sekimura, N
    Garner, FA
    EFFECTS OF RADIATION ON MATERIALS: 18TH INTERNATIONAL SYMPOSIUM, 1999, 1325 : 1109 - 1118
  • [9] Synergistic effects of hydrogen and helium on microstructural evolution in vanadium alloys by triple ion beam irradiation
    Sekimura, N
    Iwai, T
    Arai, Y
    Yonamine, S
    Naito, A
    Miwa, Y
    Hamada, S
    JOURNAL OF NUCLEAR MATERIALS, 2000, 283 (PART I) : 224 - 228
  • [10] Permeation of hydrogen through vanadium under helium ion irradiation
    Hatano, Y
    Nanjo, Y
    Hayakawa, R
    Watanabe, K
    JOURNAL OF NUCLEAR MATERIALS, 2000, 283 : 868 - 871