The pyrometallurgical recovery of zinc from electric arc furnace dust (EAFD) with active carbon

The reduction of minor impurities (e.g., Ferrite, Magnesium, Lead, Chromium) from Zinc rich-EAFD with active carbon addition was investigated at temperature between 9001300 degrees C. The result was powder with higher zinc content which then analysed by X-ray fluorescence spectroscopy (XRF), X-ray diffraction (XRD) and scanning electron microscope (SEM) equipped with X-Ray energy dispersive spectrometry (EDS). The thermogravimetry (TG) and differential thermal analysis (DTA) of EAFD and carbon mixture was conducted previously to grasp the temperature of thermic reaction of mixture. Recovery of 90wt% zinc from EAFD available was achieved up to 99.2wt% after the pyrometallurgy process at temperature 900 degrees C in atmosphere pressure while the extension of the time corresponds to the amount of recovered zinc dross.