Grain-boundary diffusion of nickel in Cr-, Fe-, and Zr-modified Ni3Al intermetallic

被引：8
|
作者：
Cermák, J [1 ]
Ruzicková, J [1 ]
Pokorná, A [1 ]
机构：
[1] Acad Sci Czech Republ, Inst Phys Mat, CZ-61662 Brno, Czech Republic
来源：
INTERMETALLICS | 1999年 / 7卷 / 06期
关键词：
aluminides; miscellaneous; diffusion; grain boundaries; structure;
D O I：
10.1016/S0966-9795(98)00089-2
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Tracer grain-boundary diffusion of Ni-63 in slightly hypostoichiometric (x(Al) < 25 at.%) Ni3Al alloys containing several percents of Cr, Fe and Zr was studied using both serial sectioning and residual activity methods. Measurements of grain-boundary diffusivity P were carried out in the temperature interval 873-1273 K. It was found that the additions of Cr, Fe and Zr decrease the P and increase the activation enthalpy of Ni-63 grain-boundary diffusion. (C) 1999 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：725 / 730
页数：6
相关论文
共 50 条
  • [1] Grain-boundary diffusion of chromium in Ni3Al intermetallic modified by Fe, Cr and Zr
    Cermak, J
    Ruzickova, J
    Pokorna, A
    INTERMETALLICS, 1998, 6 (05) : 437 - 443
  • [2] Iron grain boundary diffusion in pure and in Cr, Fe and Zr-doped Ni3Al alloys
    Stloukal, I
    Cermak, J
    Ruzicková, J
    Pokorná, A
    INTERMETALLICS, 1999, 7 (01) : 33 - 38
  • [3] Influence of boron on nickel grain boundary self-diffusion in Ni3Al intermetallic
    Cermak, J
    Stloukal, I
    Ruzickova, J
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1996, 158 (01): : 35 - 38
  • [4] GRAIN-BOUNDARY MELTING OF HAFNIUM CONTAINING NI3AL INTERMETALLIC COMPOUNDS
    CHANG, TT
    CHUANG, TH
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (06): : 763 - 768
  • [5] GRAIN-BOUNDARY STRUCTURE IN NI3AL
    MACKENZIE, RAD
    VAUDIN, MD
    SASS, SL
    JOURNAL OF METALS, 1987, 39 (10): : A38 - A38
  • [6] Grain-Boundary Self-Diffusion of Nickel in Ni3Al-Based Intermetallic Alloys
    Phys Dokl, 8 (354):
  • [7] GRAIN-BOUNDARY FRACTURE OF L12 TYPE INTERMETALLIC COMPOUND NI3AL
    OGURA, T
    HANADA, S
    MASUMOTO, T
    IZUMI, O
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (03): : 441 - 443
  • [8] GRAIN-BOUNDARY ACCOMMODATION OF SLIP IN NI3AL WITH BORON
    WEIHS, TP
    SCHULSON, EM
    FROST, HJ
    BAKER, I
    HORTON, J
    JOURNAL OF METALS, 1985, 37 (11): : A51 - A51
  • [9] Grain-boundary fracture strength in Ni3Al bicrystals
    Su, JQ
    Demura, M
    Hirano, T
    PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 2002, 82 (08): : 1541 - 1557
  • [10] ENVIRONMENTAL EMBRITTLEMENT AND GRAIN-BOUNDARY FRACTURE IN NI3AL
    LIU, CT
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (01): : 25 - 28
12345