A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime

被引：52

作者：

Ogawa, Takeshi ^{[1
]}

Stanzl-Tschegg, Stefanie E. ^{[2
]}

Schoenbauer, Bernd M. ^{[2
]}

机构：

[1] Aoyama Gakuin Univ, Dept Mech Engn, Chuo Ku, Sagamihara, Kanagawa 2525258, Japan

[2] Univ Nat Resources & Life Sci BOKU, A-1190 Vienna, Austria

来源：

ENGINEERING FRACTURE MECHANICS | 2014年 / 115卷

关键词：

Ultrasonic fatigue; Cumulative damage; Repeated two-step tests; Fish-eye fracture; Fatigue crack growth; N-GREATER-THAN-10(7) CYCLES; HIGH NUMBERS; PROPAGATION; INITIATION; STEEL; ALLOY; FAILURE; LIMIT;

D O I：

10.1016/j.engfracmech.2013.11.007

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Growth rates of optically dark areas (ODA) and fish-eyes (FE) were quantified in kHzultrasonic fatigue tests on SUJ2 and 17-4PH steels at constant and repeated two-step amplitudes. Sizes of ODAs and FEs depended on the stress intensity factor (SIF) range, and interior fatigue crack growth rates (FCGR) were slower than those of "long" cracks in air, suggesting vacuum as ODA growth environment. Repeated two-step tests on SUJ2 steel served to form beach marks so that, a quantification of ODA sizes, interior FCGRs and SIFs became possible. Additional FCGR measurements of long cracks in vacuum and comparable fracture morphologies allowed estimating the growth rates of ODAs and FEs in 17-4PH steel. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：241 / 254

页数：14

共 50 条

[1] Fracture mechanics approach to small fatigue crack growth and coalescence under low cycle fatigue
Hasunuma, Shota
Ogawa, Takeshi
Kikuchi, Masanori
[J]. Zairyo/Journal of the Society of Materials Science, Japan, 2011, 60 (12): : 1060 - 1065
[2] Crack growth behaviour of aluminium wrought alloys in the Very High Cycle Fatigue regime
Buelbuel, Fatih
Kirsten, Tina
Wicke, Marcel
Zimmermann, Martina
Brueckner-Foit, Angelika
Christ, Hans-Juergen
[J]. 12TH INTERNATIONAL FATIGUE CONGRESS (FATIGUE 2018), 2018, 165
[3] Characteristic of interior crack initiation and early growth for high cycle and very high cycle fatigue of a martensitic stainless steel
Sun, Chengqi
Song, Qingyuan
Zhou, Lingling
Pan, Xiangnan
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 758 : 112 - 120
[4] Mechanism of crack initiation and early growth of high strength steels in very high cycle fatigue regime
Song, Qingyuan
Sun, Chengqi
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 771
[5] Crack path and regularities for ball-bearing fracture in the very-high-cycle fatigue regime
Shanyavskiy, Andrey A.
Soldatenkov, Aleksey P.
[J]. Fatigue and Fracture of Engineering Materials and Structures, 2022, 45 (11): : 3378 - 3392
[6] Crack path and regularities for ball-bearing fracture in the very-high-cycle fatigue regime
Shanyavskiy, Andrey A.
Soldatenkov, Aleksey P.
[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (11) : 3378 - 3392
[7] Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion
Palin-Luc, Thierry
Perez-Mora, Ruben
Bathias, Claude
Dominguez, Gonzalo
Paris, Paul C.
Luis Arana, Jose
[J]. ENGINEERING FRACTURE MECHANICS, 2010, 77 (11) : 1953 - 1962
[8] Crack path in torsion loading in very high cycle fatigue regime
Xue, H. Q.
Bathias, C.
[J]. ENGINEERING FRACTURE MECHANICS, 2010, 77 (11) : 1866 - 1873
[9] Correlation of crack growth rate and stress ratio for fatigue damage containing very high cycle fatigue regime
Sun, Chengqi
Hong, Youshi
[J]. THEORETICAL AND APPLIED MECHANICS LETTERS, 2012, 2 (03)
[10] Interior crack initiation and growth behaviors and life prediction of a carburized gear steel under high cycle fatigue and very high cycle fatigue
Li, Wei
Sun, Zhenduo
Deng, Hailong
Zhang, Zhenyu
Sakai, Tatsuo
[J]. JOURNAL OF MATERIALS RESEARCH, 2015, 30 (14) : 2247 - 2257

← 1 2 3 4 5 →