Ultrastructural evaluation of enamel after dental bleaching associated with fluoride

This study evaluated the effects on human enamel after two bleaching procedures: with a fluoridated bleaching agent and with topical fluoride application postbleaching. It used 43 enamel blocks (3 mm2) that were ground flat (6002,000 grit) and polished with polishing paste (one and one-fourth). Specimens were randomly divided into three groups according to the bleaching procedure: (1) control group, (2) hydrogen peroxide 35% (HPF) and topical application of fluoride 1.23%, and (3) HP 38% (OP) with fluoride in its composition. Bleaching agents were used according to the manufacturer's instructions. Three methodologies were used: nanoindentation, to observe surface hardness and elastic modulus; atomic force microscopy, to observe surface roughness (Ra - Rz); and scanning electron microscopy, to observe the enamel surface effects. Group OP had a decrease in the elastic modulus after bleaching, which was recovered at 14 days. An increased roughness (Ra; 32%) was observed on group HPF and had an increased erosion on enamel surface (67%). It was concluded that topical application of fluoride, after using the nonfluoridated whitening agent, increased the roughness values and erosion of enamel. Microsc. Res. Tech. 75:10931098, 2012. (c) 2012 Wiley Periodicals, Inc.