Composition design and microstructure characterization of Zr-Al-Ni-Cu bulk amorphous alloys

被引:0
|
作者
Chen, WR [1 ]
Wang, YM
Qiang, JB
Dong, C
机构
[1] Dalian Univ Technol, Dept Mat Engn, Dalian 116024, Peoples R China
[2] Dalian Univ Technol, Dept Mech Engn, Dalian 116622, Peoples R China
关键词
Zr base amorphous alloy; electron concentration; atomic size;
D O I
暂无
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Six bull, metallic glass alloys of Zr-Al-Ni-Cu with different compositions were designed according to electron concentration constant and atomic size constant criteria. The cylindrical ingots with top diameter of 3 mm and bottom diameter of 4 mm and length of 30 mm are prepared by suction casting into copper mould. All the samples are mainly in glassy state with large supercooled liquid ranges, high glass transition temperatures and high reduced glass transition temperatures as revealed by DSC and DTA curves. Only two samples with Cu content greater than or equal to 20 (atomic fraction, %) contain a small amount of crystalline phases as proved by XRD and TEAL It is also shown that different phases form at the top and bottom ends of the ingots due to different cooling conditions.
引用
收藏
页码:421 / 426
页数:6
相关论文
共 17 条
  • [1] THERMODYNAMIC CONSIDERATIONS ON FORMATION AND STABILITY OF METALLIC GLASSES
    CHEN, HS
    [J]. ACTA METALLURGICA, 1974, 22 (12): : 1505 - 1511
  • [2] On the effect of the number of components on glass-forming ability of alloys from the liquid state: Application to the new generation of multicomponent bulk glasses
    Desre, PJ
    [J]. MATERIALS TRANSACTIONS JIM, 1997, 38 (07): : 583 - 588
  • [3] DONG C, 1994, MATER SCI FORUM, V150, P151
  • [4] INONE A, 1993, MATER T JIM, V34, P1234
  • [5] GLASS-FORMING ABILITY OF ALLOYS
    INOUE, A
    ZHANG, T
    MASUMOTO, T
    [J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1993, 156 : 473 - 480
  • [6] Synthesis of high strength bulk amorphous Zr-Al-Ni-Cu-Ag alloys with a nanoscale secondary phase
    Inoue, A
    Zhang, T
    Kim, YH
    [J]. MATERIALS TRANSACTIONS JIM, 1997, 38 (09): : 749 - 755
  • [7] ZR-AL-NI AMORPHOUS-ALLOYS WITH HIGH GLASS-TRANSITION TEMPERATURE AND SIGNIFICANT SUPERCOOLED LIQUID REGION
    INOUE, A
    ZHANG, T
    MASUMOTO, T
    [J]. MATERIALS TRANSACTIONS JIM, 1990, 31 (03): : 177 - 183
  • [8] Fabrication of bulk glassy Zr55Al10Ni5Cu30 alloy of 30 mm in diameter by a suction casting methodQ
    Inoue, A
    Zhang, T
    [J]. MATERIALS TRANSACTIONS JIM, 1996, 37 (02): : 185 - 187
  • [9] Fundamental aspects of bulk metallic glass formation in multicomponent alloys
    Johnson, WL
    [J]. METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2, 1996, 225 : 35 - 49
  • [10] Formation of quasicrystals in bulk glass forming Zr-Cu-Ni-Al alloys
    Koster, U
    Meinhardt, J
    Roos, S
    Busch, R
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 226 : 995 - 998