Microstructural development and solidification cracking susceptibility of a stabilized stainless steel

被引：1

作者：

DuPont, JN ^{[1
]}

机构：

[1] Lehigh Univ, Dept Mat Sci & Engn, Bethlehem, PA 18015 USA

来源：

WELDING JOURNAL | 1999年 / 78卷 / 07期

关键词：

alloy; 20; Cb-3; E320LR; INCO; 112; Laves phase; maximum crack length; stainless steel; solidification cracking; Varestraint testing;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

引用

页码：253S / 263S

页数：11

共 50 条

[1] MICROSTRUCTURAL DEVELOPMENT AND SOLIDIFICATION CRACKING SUSCEPTIBILITY OF AUSTENITIC STAINLESS-STEEL WELDS
BROOKS, JA
THOMPSON, AW
[J]. INTERNATIONAL MATERIALS REVIEWS, 1991, 36 (01) : 16 - 44
[2] Microstructural development and solidification cracking susceptibility of Cu deposits on steel: Part I
Noecker, Fredrick F., II
DuPont, John N.
[J]. JOURNAL OF MATERIALS SCIENCE, 2007, 42 (02) : 495 - 509
[3] Microstructural evolution and solidification cracking susceptibility of grain boundary engineered fully austenitic stainless steel
Tokita, Shun
Kadoi, Kota
Kanno, Yudai
Inoue, Hiroshige
[J]. WELDING IN THE WORLD, 2020, 64 (04) : 593 - 600
[4] Microstructural evolution and solidification cracking susceptibility of grain boundary engineered fully austenitic stainless steel
Shun Tokita
Kota Kadoi
Yudai Kanno
Hiroshige Inoue
[J]. Welding in the World, 2020, 64 : 593 - 600
[5] Effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
[J]. Liu, R. (lrp_msc@nuaa.edu.cn), 2005, China Welding (14):
[6] Influence mechanism of solidification mode on solidification cracking susceptibility of stainless steel
Yamashita, Shotaro
Yamauchi, Ryohei
Saida, Kazuyoshi
[J]. WELDING INTERNATIONAL, 2022, 36 (11) : 693 - 704
[7] The effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
刘仁培
董祖珏
潘永明
[J]. China Welding, 2005, (01) : 38 - 43
[8] Microstructural development and solidification cracking susceptibility of Cu deposits on steel: Part II—use of a Ni interlayer
Fredrick F. Noecker
John N. DuPont
[J]. Journal of Materials Science, 2007, 42 : 510 - 521
[9] MICROSTRUCTURAL DEVELOPMENT DURING SOLIDIFICATION OF STAINLESS-STEEL ALLOYS
ELMER, JW
ALLEN, SM
EAGAR, TW
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10): : 2117 - 2131
[10] Solidification Cracking Susceptibility Predictions for Stainless Steels
Soysal, Tayfun
Erk, Berke
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 32 (17) : 7991 - 7997

← 1 2 3 4 5 →