Influence of Dynamic Strain Aging on High Cycle Fatigue Behavior of Alloy 617M

被引：14
|
作者：
Sarkar, Aritra [1 ]
Nagesha, A. [1 ]
Sandhya, R. [1 ]
Nandagopal, M. [1 ]
Laha, K. [1 ]
Bhaduri, A. K. [1 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Met & Mat Grp, Kalpakkam 603102, Tamil Nadu, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2016年 / 69卷 / 02期
关键词：
DSA; HCF; Alloy; 617M;
D O I：
10.1007/s12666-015-0748-9
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Effect of dynamic strain aging (DSA) on the high cycle fatigue (HCF) behavior of alloy 617M was evaluated at ambient temperature and 923 K. The material showed finite cyclic lives at stresses below the yield stress (YS) at ambient temperature. However, tests conducted at 923 K which distinctly falls under the DSA regime, led to run-out (10(7) cycles) at stresses below and at YS. Experimental results also indicated that fatigue limit (based on run-out at 10(7) cycles) exceeded the YS at 923 K. This indicates that under HCF loading, fatigue failure is suppressed under the influence of DSA which in turn shifts the window of finite lives to higher stresses even above YS.
引用
收藏
页码：399 / 402
页数：4
相关论文
共 50 条
  • [1] Influence of Dynamic Strain Aging on High Cycle Fatigue Behavior of Alloy 617M
    Aritra Sarkar
    A. Nagesha
    R. Sandhya
    M. Nandagopal
    K. Laha
    A. K. Bhaduri
    [J]. Transactions of the Indian Institute of Metals, 2016, 69 : 399 - 402
  • [2] Occurrence of dynamic strain aging in Alloy 617M under low cycle fatigue loading
    Shankar, Vani
    Kumar, Amit
    Mariappan, K.
    Sandhya, R.
    Laha, K.
    Bhaduri, A. K.
    Narasaiah, N.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2017, 100 : 12 - 20
  • [3] Strain Amplitude and Temperature Effects on the Low Cycle Fatigue Behavior of Alloy 617M
    Mariappan, K.
    Shankar, Vani
    Goyal, Sunil
    Sandhya, R.
    Laha, K.
    Bhaduri, A. K.
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (02) : 325 - 329
  • [4] Low Cycle Fatigue Behavior of Forged Alloy 617M
    J. Veerababu
    R. Kannan
    Sunil Goyal
    A. Nagesha
    [J]. Transactions of the Indian National Academy of Engineering, 2022, 7 (2) : 417 - 424
  • [5] Strain Amplitude and Temperature Effects on the Low Cycle Fatigue Behavior of Alloy 617M
    K. Mariappan
    Vani Shankar
    Sunil Goyal
    R. Sandhya
    K. Laha
    A. K. Bhaduri
    [J]. Transactions of the Indian Institute of Metals, 2016, 69 : 325 - 329
  • [6] High-Temperature Fatigue Behaviour of Alloy 617M
    Sandeep Kale
    M. M. Thawre
    Atul Ballal
    D. R. Peshwe
    Abhilasha Jain
    Priyadarshini Bais
    Aritra Sarkar
    A. Nagesha
    [J]. Transactions of the Indian National Academy of Engineering, 2022, 7 (2) : 685 - 688
  • [7] A re-visit to the Haigh diagram with the effect of creep damage on the high cycle fatigue behavior of alloy 617M
    Ponnapureddy, Shiven
    Sarkar, Aritra
    Nagesha, A.
    Narasaiah, N.
    Rao, Bonta Srinivasa
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2021, 149
  • [8] Influence of Dynamic Strain Aging on Tensile Deformation Behavior of Alloy 617
    Ekaputra, I. M. W.
    Kim, Woo-Gon
    Park, Jae-Young
    Kim, Seon-Jin
    Kim, Eung-Seon
    [J]. NUCLEAR ENGINEERING AND TECHNOLOGY, 2016, 48 (06) : 1387 - 1395
  • [9] Microstructural damage assessment in alloy 617M near high cycle fatigue threshold at elevated temperature
    Kale, Sandeep
    Thawre, M. M.
    Peshwe, D. R.
    Nagesha, A.
    Sarkar, Aritra
    Dandekar, Tushar R.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (04) : 1445 - 1465
  • [10] Evaluation of of high cycle fatigue behaviour of alloy 617M at 973 K: Haigh diagram and associated mechanisms
    Karnati, Abhinav Kumar
    Sarkar, Aritra
    Nagesha, A.
    Parameswaran, P.
    Sandhya, R.
    Narasaiah, N.
    [J]. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2019, 172 : 304 - 312
12345