Irradiation induced densification and its correlation with three-membered rings in vitreous silica

Suprasil silica glass was irradiated by 50 key electron beam with doses within the range of 3.1-191.1 kC/m(2). Volume changes induced by electron irradiation were monitored by means of Atomic Force Microscopy (AFM). Raman spectra were taken from irradiated spots to observe structural changes. Irradiated glasses were annealed at temperatures 500-1000 degrees C. After annealing irradiated spots were again examined by AFM and Raman spectroscopy in order to observe volume and structural relaxation of radiation-induced changes. Electron beam caused volume compaction that was correlated with D2 peak area for lower doses. D2 peak evolution under irradiation and subsequent annealing showed that topological changes in glass structure are possible deeply below the glass transition temperature. (C) 2015 Elsevier ay. All rights reserved.