Silver nanoparticles generated by pulsed laser ablation in supercritical CO2 medium

Pulsed laser ablation (PLA) has been widely employed in industrial and biological applications and in other fields. The environmental conditions in which PLA is conducted are important parameters that affect both the solid particle cloud and the deposition produced by the plume. In this work, the generation of nanoparticles (NPs) has been developed by performing PLA of silver (Ag) plates in a supercritical CO2 medium. Ag NPs were successfully generated by allowing the selective generation of clusters. Laser ablation was performed with an excitation wavelength of 532 nm under various pressures and temperatures of CO2 medium. On the basis of the experimental result, both surface of the irradiated Ag plate and structure of Ag NPs were significantly affected by the changes in supercritical CO2 pressure and temperature. With increasing irradiation pressure, plume deposited in the surrounding crater created by the ablation was clearly observed. In Field Emission Scanning Electron Microscopy (FE-SEM) the image of the generated Ag NPs on the silicon wafer and the morphology of Ag particles were basically a sphere-like structure. Ag particles contain NPs with large-varied diameter ranging from 5 nm to 1.2 mu m. The bigger Ag NPs melted during the ablation process and then ejected smaller spherical Ag NPs, which formed nanoclusters attached on the molten Ag NPs. The smaller Ag NPs were also formed around the bigger Ag NPs. Based on the results, this new method can also be used to obtain advanced nano-structured materials.