Influence of the feedstock characteristics on the microstructure and properties of Al2O3-TiO2 plasma-sprayed coatings

Atmospheric plasma spraying CAPS) is an interesting technique to obtain nanostructured coatings due to its versatility, simplicity and relatively low cost. However, nanometric powders cannot be fed into the plume using conventional feeding systems, due to their low mass and poor flowability, and must be adequately reconstituted into sprayable micrometric agglomerates. In this work, Al2O3-13 wt.%TiO2 nanostructured and submicron-nanostructured powders were deposited using APS. The feedstocks were obtained by spray drying from two starting suspensions, prepared by mixing two commercial nanosuspensions of Al2O3 and TiO2, or by adding nanosized TiO2 and submicron-sized Al2O3 powders to water. The spray-dried granules were heat-treated to reduce their porosity and the resultant powders were fully characterized. Optimization of the deposition conditions enabled the reconstituted powders to be successfully deposited, yielding coatings that were well bonded to the substrate. The coating microstructure, characterized by SEM, was formed by semi-molten feedstock agglomerates surrounded by fully molten particles that act as a binder. Moreover, microhardness, adhesion, and tribological behavior were determined, and the impact of the granule characteristics on these properties was studied. It was found that changing the feedstock characteristics allowed controlling the coating quality and properties. (C) 2012 Elsevier B.V. All rights reserved.