POWDER INJECTION MOLDING OF COPPER AND THE EFFECT OF SINTERING TEMPERATURE ON ITS MECHANICAL PROPERTIES

In this article, the fabrication steps of copper parts, using the powder injection molding method have been investigated. For the purpose of this study, first, several feedstocks were prepared by mixing copper powder (in volume percentages of 60, 64, 68, and 72%) and a thermoplastic binder. Due to the sensitivity of the mixing stage in the powder injection molding process, the Extrumixing method was utilized to appropriately mix the copper powder with the binder. Rheological characteristics of the different feedstocks were analyzed by means of a capillary rheometer. Based on this analysis, the feedstock having a 68 vol. % copper powder was selected as the optimum powder, out of which, samples shaped like tensile test specimens were successfully molded. These samples were later debinded by the solvent debinding method. Sintering of the pieces was carried out at different temperatures. Research showed that raising the sintering temperature leads to an increase of density and tensile strength of the specimens.