An investigation on hot corrosion behavior of YSZ-Ta2O5 in Na2SO4+V2O5 salt at 1100 °C

被引：89
|
作者：
Habibi, M. H. [1 ]
Wang, Li [1 ]
Liang, Jiandong [1 ]
Guo, S. M. [1 ]
机构：
[1] Louisiana State Univ, Baton Rouge, LA 70803 USA
来源：
CORROSION SCIENCE | 2013年 / 75卷
关键词：
Thermal barrier coating (TBC); YSZ; Tantalum oxide; Hot corrosion; THERMAL BARRIER COATINGS; YTTRIA; YSZ; DEGRADATION; RESISTANCE; STABILITY; CERIA; EVOLUTION; LAYER;
D O I：
10.1016/j.corsci.2013.06.025
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study compares the hot corrosion performance of yttria stabilized zirconia (YSZ), and YSZ-Ta2O5 (TaYSZ) composite samples in the presence of molten mixture of Na2SO4 + V2O5 at 1100 degrees C. For YSZ, the reaction between NaVO3 and Y2O3 produces YVO4 and leads to the transformation of tetragonal ZrO2 to monoclinic ZrO2. For TaYSZ, minor amounts of NaTaO3, TaVO5 and Ta9VO25 are formed as the hot corrosion products with only traceable amounts of YVO4. Due to the synergic effect of doping of zirconia with both Y2O3 and Ta2O5, the TaYSZ sample has a much better hot corrosion resistance than YSZ. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：409 / 414
页数：6
相关论文
共 50 条
  • [1] Evolution of Hot Corrosion Behavior of YSZ-Ta2O5 Composites with Different YSZ/Ta2O5 Ratios
    Habibi, Hamed
    Guo, Shengmin
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2015, 12 (03) : 542 - 550
  • [2] INVESTIGATION OF HOT CORROSION RESISTANCE OF PLASMA SPARAYED YSZ-CERIA TBC IN Na2SO4+V2O5 AT 1050 °C
    Saremi, M.
    Habibi, M. H.
    TMS2011 SUPPLEMENTAL PROCEEDINGS, VOL 1: MATERIALS PROCESSING AND ENERGY MATERIALS, 2011, : 429 - 437
  • [3] Effects of sintering additives on hot corrosion behavior of γ-Y2Si2O7 ceramics in Na2SO4+V2O5 molten salt
    Fan, Xingyu
    Sun, Runjun
    Dong, Jie
    Wei, Liang
    Wang, Qiushi
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2021, 41 (01) : 517 - 525
  • [4] Hot corrosion behavior of nanostructured Gd2O3 doped YSZ thermal barrier coating in presence of Na2SO4+V2O5 molten salts
    Yixiong Wang
    Chungen Zhou
    ProgressinNaturalScience:MaterialsInternational, 2017, 27 (04) : 507 - 513
  • [5] Thermal corrosion behavior of Yb4Hf3O12 exposed to Na2SO4+V2O5 molten salt
    Li, Yang
    Sun, Zhipeng
    He, Ling
    Pan, Ling
    Xiao, Peng
    Zhu, Henghai
    Duan, Junjie
    Zhou, Wei
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1008
  • [6] Thermal corrosion behavior of Yb4Hf3O12 exposed to Na2SO4+V2O5 molten salt
    Li, Yang
    Sun, Zhipeng
    He, Ling
    Pan, Ling
    Xiao, Peng
    Zhu, Henghai
    Duan, Junjie
    Zhou, Wei
    Journal of Alloys and Compounds, 1600, 1008
  • [7] Hot corrosion behavior of the La2(Zr0.7Ce0.3)2O7 ceramic in molten V2O5 and a Na2SO4+V2O5 salt mixture
    Yin, Yichuan
    Ma, Wen
    Jin, Xilong
    Li, Xiaoying
    Bai, Yu
    Jia, Ruiling
    Dong, Hongying
    JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 689 : 123 - 129
  • [8] Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4 + V2O5 or V2O5 salt at 900 °C
    Wang, Xizhong
    Guo, Lei
    Peng, Hui
    Zheng, Lei
    Guo, Hongbo
    Gong, Shengkai
    CERAMICS INTERNATIONAL, 2015, 41 (05) : 6604 - 6609
  • [9] Phase stability and hot corrosion behavior of ZrO2-Ta2O5 compound in Na2SO4-V2O5 mixtures at elevated temperatures
    Habibi, M. H.
    Yang, Shizhong
    Guo, S. M.
    CERAMICS INTERNATIONAL, 2014, 40 (03) : 4077 - 4083
  • [10] Hot Corrosion Behavior of Inconel 625 in Na2SO4 and V2O5 Molten Salt System
    Li, Liang
    Li, Lanfeng
    Zhang, Guofeng
    Xue, Hongdi
    Cui, Maomao
    Wang, Wenxu
    Liu, Dexue
    METALS, 2023, 13 (06)
12345