Influence of CoO and Al2O3 on the phase partitioning of ZrO2-3 mol% Y2O3

被引：8
|
作者：
Chiou, YH
Lin, ST
机构：
[1] Mechanical Engineering Department, Natl. Taiwan Institute of Technology, Taipei
来源：
CERAMICS INTERNATIONAL | 1996年 / 22卷 / 03期
关键词：
D O I：
10.1016/0272-8842(95)00100-X
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Tetragonal zirconia polycrystal doped with 1.5 wt% CoO and 1.5 wt% Al2O3 showed large and faceted CoAl2O4 spinel grains existing in clusters and large monoclinic zirconia grains. Major stages of microstructural evolution during sintering included (1) formation of spinel as a result of preferred segregation of CoO to Al2O3 phase, (2) exudation of liquid phase to grain junctions among faceted spinel grains and zirconia grains, and (3) growth of spinel grains and the zirconia grains adjacent to the spinel phase.
引用
收藏
页码：249 / 256
页数：8
相关论文
共 50 条
  • [1] Electric response of ZrO2-3 mol% Y2O3 nanocrystals
    Cachadiña, I
    Solier, JD
    Sánchez-Bajo, F
    Domínguez-Rodríguez, YA
    BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 1999, 38 (06): : 611 - 614
  • [2] Rapid rate sintering of nanocrystalline ZrO2-3 mol% Y2O3
    Pennsylvania State Univ, University Park, United States
    J Am Ceram Soc, 4 (906-912):
  • [3] Synthesis and sintering behavior of nanocrystalline ZrO2-3 mol% Y2O3 powders
    Srdic, Vladimir V.
    Radonjic, Ljiljana
    Key Engineering Materials, 1997, 132-136 (Pt 1): : 45 - 48
  • [4] Effect of Al2O3 on the properties of nanocrystalline ZrO2 + 3 mol % Y2O3 powder
    E. V. Dudnik
    A. V. Shevchenko
    A. K. Ruban
    V. P. Red’ko
    L. M. Lopato
    Inorganic Materials, 2010, 46 : 172 - 176
  • [5] Effect of Al2O3 on the properties of nanocrystalline ZrO2+3 mol % Y2O3 powder
    Dudnik, E. V.
    Shevchenko, A. V.
    Ruban, A. K.
    Red'ko, V. P.
    Lopato, L. M.
    INORGANIC MATERIALS, 2010, 46 (02) : 172 - 176
  • [6] Microstructure Evolution During Spark Plasma Sintering of Metastable (ZrO2-3 mol% Y2O3)-20 wt% Al2O3 Composite Powders
    Suffner, Jens
    Lattemann, Martina
    Hahn, Horst
    Giebeler, Lars
    Hess, Christian
    Garcia Cano, Irene
    Dosta, Sergi
    Maria Guilemany, Josep
    Musa, Clara
    Locci, Antonio Mario
    Licheri, Roberta
    Orru, Roberto
    Cao, Giacomo
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2010, 93 (09) : 2864 - 2870
  • [7] Characterization of heterogeneous microstructure evolution in ZrO2-3 mol%Y2O3 during isothermal sintering
    Nettleship, Ian
    Chen, Tiandan
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (12) : 3793 - 3799
  • [8] The ceramic ZrO2-3 mol.% Y2O3 formed by sintering and its behavior at fracture
    Konstantinova, TE
    Danilenko, IA
    Gorokh, AV
    Volkova, GK
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2001, 42 (3-4) : 102 - 105
  • [9] Influences of powder preparation routes on the sintering behaviour of doped ZrO2-3 mol%Y2O3
    Chiou, YH
    Lin, ST
    CERAMICS INTERNATIONAL, 1997, 23 (02) : 171 - 177
  • [10] MICROSTRUCTURE OF ZRO2-2.5MOL-PERCENT-Y2O3-8.5MOL-PERCENT-AL2O3 IN DIRECTIONALLY SOLIDIFIED AL2O3-ZRO2(Y2O3) EUTECTIC
    ECHIGOYA, J
    SUTO, H
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1986, 5 (09) : 949 - 950
12345