Coexistence of localized and (induced) itinerant magnetism and heat-capacity anomalies in Gd1-xYxNi alloys

The results of magnetization (M), electrical resistivity (rho), and heat-capacity (C) measurements for the alloys, Gd1-xYxNi, are reported. The x-ray-diffraction patterns indicate that there is a change in the crystal structure from CrB-type to FeB-type orthorhombic structure for increasing x near n=0.4. GdNi has been known to order ferromagnetically at 70 K and the observed x dependence of T-C and theta(p) proves that the strength of Gd-Gd exchange interaction is enhanced by a factor of about 1.5 in the FeB structure. The M data suggest that there is an excess moment for the Gd-rich alloys. The observed magnetization behavior is taken as an evidence to show that there is coexistence of localized magnetism (from Gd) and itinerant ferromagnetism of induced-type, presumably from Ni 3d band. There is an enhancement of C with decreasing temperature above T-C over a wide temperature range presumably due to short-range order effects in these alloys.