Synthesis and characterization of LaPO4-coated α-Al2O3 powders

被引:11
|
作者
Zheng, Qiuju [1 ]
Wang, Xin [1 ]
Tian, Jintao [1 ]
Liu, Zifeng [1 ]
Huang, Chuanshun [1 ]
Wang, Jing [1 ]
Xu, Jihui [1 ]
机构
[1] Ocean Univ China, Inst Mat Sci & Engn, Qingdao 266100, Peoples R China
关键词
Powders: chemical preparatiom; Composite; Chemical properties Heterogeneous nucleation processing; HETEROGENEOUS NUCLEATION; MICROSTRUCTURE; COMPOSITE; MONAZITE; BEHAVIOR; ALUMINA; GROWTH;
D O I
10.1016/j.ceramint.2008.03.014
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
LaPO4-coated alpha-Al2O3 powders were successfully synthesized through the heterogeneous precipitation method. The coated powders were characterized by XRD, TEM. EDS, and zeta-potential measurements. According to the XRD results, the coated powders consisted of only alpha-Al2O3 and monoclinic LaPO4. The TEM examinations and EDS analysis showed that under alkaline condition a homogeneous coating with thickness of similar to 10 nm was obtained on the alpha-Al2O3 powder surface. The zeta-potential measurements showed the coated powders to have a pH value of 7.85 at isoelectric point, similar to that of LaPO4 (pH value of 8.21). This was in good agreement with the TEM and EDS results, indicating a successful coating process in our experiment. (C) 2008 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码:897 / 900
页数:4
相关论文
共 50 条
  • [1] Preparation and characterization of Al2O3 coated graphite powders
    Wang, ZF
    Wang, HZ
    Hong, YR
    Deng, CG
    HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2, 2005, 280-283 : 1671 - 1674
  • [2] Synthesis and properties of CaAl2O4-coated Al2O3 microcomposite powders
    Univ of Illinois at Urbana-Champaign, Urbana, United States
    J Am Ceram Soc, 11 (2881-2888):
  • [3] SYNTHESIS AND PROPERTIES OF CAAL2O4-COATED AL2O3 MICROCOMPOSITE POWDERS
    DESAI, PG
    XU, ZK
    LEWIS, JA
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (11) : 2881 - 2888
  • [4] Ni-coated Al2O3 powders
    Li, GJ
    Huang, XX
    Guo, JK
    Chen, DM
    CERAMICS INTERNATIONAL, 2002, 28 (06) : 623 - 626
  • [5] Oxide composites of Al2O3 and LaPO4
    Davis, JB
    Marshall, DB
    Morgan, PED
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (13-14) : 2421 - 2426
  • [6] Synthesis and Photoluminescence of γ-Al2O3 and C-doped γ-Al2O3 Powders
    Wang, S. F.
    Zhuang, C. F.
    Yuan, Y. G.
    Xiang, X.
    Sun, G. Z.
    Ding, Q. P.
    Li, Z. J.
    Zu, X. T.
    TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY, 2014, 73 (01) : 37 - 42
  • [7] LaPO4-containing machinable Al2O3 ceramics
    Hikichi, Y
    Daimon, K
    Ota, T
    PHOSPHORUS SULFUR AND SILICON AND THE RELATED ELEMENTS, 2002, 177 (8-9) : 1915 - 1915
  • [8] Ultrasonic machining of Al2O3/LaPO4 composites
    Majeed, M. Abdul
    Vijayaraghavan, L.
    Malhotra, S. K.
    Krishnamurthy, R.
    INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 2008, 48 (01): : 40 - 46
  • [9] Synthesis and characterization of Al2O3/SiC powders from natural aluminosilicates
    Borsa, CE
    Spiandorello, FM
    Kiminami, RHGA
    ADVANCED POWDER TECHNOLOGY, 1999, 299-3 : 57 - 62
  • [10] Characteristics of machinable LaPO4/Al2O3 composites
    Jiang, M
    Liu, JC
    Du, HY
    Liu, YR
    Cao, ZJ
    HIGH-PERFORMANCE CERAMICS III, PTS 1 AND 2, 2005, 280-283 : 1087 - 1088