Study on the Hot Deformation Behavior and Microstructure Evolution of Cu-Cr-In Alloy

Based on the hot compressive tests in the temperature range of 700-900 degrees C and strain rate range of 0.01-10s(-1), the hot deformation behavior of a Cu-Cr-In alloy was investigated. The true stress-strain curves of the alloy were obtained, and a constitutive equation for the alloy was established by the method of equivalent stress. The processing maps were constructed based on the constitutive equation, and the microstructural evolutions were analyzed and correlated with the processing maps. The results show that the true stress of the alloy increased with decreasing strain rate and decreased with increasing temperature. The microstructures of the alloy deformed under different conditions were in good accordance with the processing maps results. According to the processing maps and the microstructures of the alloy with true strains of 0.4 and 0.8, the optimal hot deformation conditions lie in the range of 850-900 degrees C and strain rate range of 0.01-0.1s(-1).