The effects of the micrometric and nanometric iron (Fe) additives on the mechanical and thermal dehydrogenation of lithium alanate (LiAlH4), its self-discharge at low temperatures and rehydrogenation

被引:44
|
作者
Varin, Robert A. [1 ]
Parviz, Roozbeh [1 ]
机构
[1] Univ Waterloo, Dept Mech & Mechatron Engn, WIN, Waterloo, ON N2L 3G1, Canada
基金
加拿大自然科学与工程研究理事会;
关键词
Solid state hydrogen storage; Lithium alanate (LiAlH4); Micrometric and nanometric iron; Ball milling energy; Dehydrogenation and rehydrogenation; REVERSIBLE HYDROGEN STORAGE; TI-DOPED LIALH4; SODIUM; DECOMPOSITION; CATALYST; RELEASE; TRANSFORMATIONS; BEHAVIOR;
D O I
10.1016/j.ijhydene.2012.02.182
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
LiAlH4 containing 5 wt.% of nanometric Fe (n-Fe) shows a profound mechanical dehydrogenation by continuously desorbing hydrogen (H-2) during high energy ball milling reaching similar to 3.5 wt.% H-2 after 5 h of milling. In contrast, no H-2 desorption is observed during low energy milling of LiAlH4 containing n-Fe. Similarly, no H-2 desorption occurs during high energy ball milling for LiAlH4 containing micrometric Fe (mu-Fe) and, for comparison, both the micrometric and nanometric Ni (mu-Ni and n-Ni) additive. X-ray diffraction studies show that ball milling results in a varying degree of the lattice expansion of LiAlH4 for both the Fe and Ni additives. A volumetric lattice expansion larger than 1% results in the profound destabilization of LiAlH4 accompanied by continuous H-2 desorption during milling according to reaction: LiAlH4 (solid) -> 1/3Li(3)AlH(6) + 2/3Al + H-2. It is hypothesized that the Fe ions are able to dissolve in the lattice of LiAlH4 by the action of mechanical energy, replacing the Al ions and forming a substitutional solid solution. The quantity of dissolved metal ions depends primarily on the total energy of milling per unit mass of powder generated within a prescribed milling time, the type of additive ion e.g. Fe vs. Ni and on the particle size (micrometric vs. nanometric) of metal additive. For thermal dehydrogenation the average apparent activation energy of Stage I (LiAlH4 (solid) -> 1/3Li(3)AlH(6) + 2/3Al + H-2) is reduced from the range 76 to 96 kJ/mol for the mu-Fe additive to about 60 kJ/mol for the n-Fe additive. For Stage II dehydrogenation (1/3Li(3)AlH(6) -> LiH+1/3Al + 0.5H(2)) the average apparent activation energy is within the range 77-93 kJ/mol, regardless of the particle size of the Fe additive (mu-Fe vs. n-Fe). The n-Fe and n-Ni additives, the latter used for comparison, provide nearly identical enhancement of dehydrogenation rate during isothermal dehydrogenation at 100 degrees C. Ball milled (LiAlH4 + 5 wt.% n-Fe) slowly self-discharges up to similar to 5 wt.% H-2 during storage at room temperature (RT), 40 and 80 degrees C. Fully dehydrogenated (LiAlH4 + 5 wt.% n-Fe) has been partially rehydrogenated up to 0.5 wt.% H-2 under 100 bar/160 degrees C/24 h. However, the rehydrogenation parameters are not optimized yet. Copyright (C) 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.