Effect of Heat Treatment on Corrosion, Fatigue, and Corrosion Fatigue Behavior of 17-4PH Stainless Steel

被引：4

作者：

Malakshah, M. Ghasemian ^{[1
]}

Eslami, A. ^{[1
]}

Ashrafizadeh, F. ^{[1
]}

Berenjkoub, A. ^{[1
]}

机构：

[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2023年 / 32卷 / 15期

关键词：

17-4PH stainless steel; corrosion; corrosion fatigue; fatigue; heat treatment; MICROSTRUCTURE;

D O I：

10.1007/s11665-022-07614-6

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This study investigates effect of heat treatment on fatigue and corrosion fatigue resistance of 17-4PH stainless steel at two thermal cycles, which consisted of 30 min solution annealing at 1050 C and 240 min ageing at 620 C as an overaged thermal cycle, and heat treatment at 464 C for 129 min as an optimized aged thermal cycle. Microstructural characteristics, tensile and hardness properties, corrosion performance, Hydrogen permeation, fatigue and corrosion fatigue resistance of these samples were then compared. Results showed that corrosion resistance and fatigue resistance of aged 17-4PH stainless steel was superior. Despite this, the corrosion fatigue resistance of the heat-treated steels was a function of applied loads and their exposure time to the corrosive environment. In fact, for the lower applied loads/longer exposure times, the overaged steel with higher corrosion rate, and less susceptibility to hydrogen damage had better corrosion fatigue performance, than the aged 17-4PH stainless steel.

引用

页码：6610 / 6621

页数：12

共 50 条

[1] Effect of Heat Treatment on Corrosion, Fatigue, and Corrosion Fatigue Behavior of 17-4PH Stainless Steel
M. Ghasemian Malakshah
A. Eslami
F. Ashrafizadeh
A. Berenjkoub
[J]. Journal of Materials Engineering and Performance, 2023, 32 : 6610 - 6621
[2] Effect of Aging Heat Treatment on Corrosion Behavior and Corrosion Kinetics of 17-4PH Stainless Steel in Artificial Saliva
Kosasang, Onthida
Wongkaewmoon, Manutchaya
Chumphongphan, Somwan
[J]. SAINS MALAYSIANA, 2021, 50 (03): : 849 - 858
[3] Corrosion fatigue behavior of 17-4 PH stainless steel in different tempers
Lin, CK
Lin, CP
[J]. FATIGUE AND FRACTURE MECHANICS: 33RD VOLUME, 2003, 1417 : 598 - 613
[4] Effect of aging heat treatment on microbiologically influenced corrosion of 17-4PH stainless steel by Pseudomonas aeruginosa
Zhao, Li
Qian, Hongchang
Chang, Weiwei
Guo, Dawei
Kwok, Chi Tat
Tam, Lap Mou
Zhang, Dawei
[J]. CORROSION SCIENCE, 2024, 227
[5] Inhibitive Effect of Nitrate on Pitting Corrosion of 17-4PH Stainless Steel
Seyedi, M.
Mirjalili, M.
Taji, I.
Armat, O.
Moayed, M. H.
[J]. CORROSION, 2017, 73 (02) : 181 - 191
[6] Effect of different heat-treatment processes on corrosion resistance of 17-4PH steel
Chen, Xiaoqin
Qin, Xiaofei
Li, Yue
Cheng, Wenjia
Jin, Haonan
Li, Quan
[J]. BULLETIN OF MATERIALS SCIENCE, 2024, 47 (04)
[7] Pitting corrosion behavior of friction-surfaced 17-4PH stainless steel coatings with and without subsequent heat treatment
Guo, D.
Chen, J.
Chen, X.
Shi, Q.
Cristino, V. A. M.
Kwok, C. T.
Tam, L. M.
Qian, H.
Zhang, D.
Li, X.
[J]. CORROSION SCIENCE, 2021, 193
[8] Effect of hydrostatic pressure on the pitting corrosion of 17-4PH martensitic stainless steel
Ma, Hongyu
Liu, Rui
Ke, Peiling
Cui, Yu
Liu, Li
Wang, Fuhui
[J]. ENGINEERING FAILURE ANALYSIS, 2022, 138
[9] The influence of corrosion pits on the fatigue life of 17-4PH steam turbine blade steel
Schoenbauer, Bernd M.
Stanzl-Tschegg, Stefanie E.
Perlega, Andrea
Salzman, Ronald N.
Rieger, Neville F.
Turnbull, Alan
Zhou, Shengqi
Lukaszewicz, Mikolaj
Gandy, David
[J]. ENGINEERING FRACTURE MECHANICS, 2015, 147 : 158 - 175
[10] EFFECT OF HEAT-TREATMENT ON CORROSION-FATIGUE CRACK GROWTH IN 17-4 PH STEEL
CROOKER, TW
CARES, WR
[J]. REPORT OF NRL PROGRESS, 1974, (MAR): : 39 - 41

← 1 2 3 4 5 →