Phase equilibria in Zn-Nb-Ti ternary system at 600 and 450 °C

被引：0
|
作者：
Long, Zhaohui [1 ,2 ]
Li, Jiafeng [1 ]
Gong, Weiping [2 ]
Yang, Shan [1 ]
Yin, Fucheng [1 ]
机构：
[1] Xiangtan Univ, Sch Mat Sci & Engn, Xiangtan 411105, Hunan, Peoples R China
[2] Huizhou Univ, Guangdong Prov Key Lab Elect Funct Mat & Devices, Huizhou 516001, Guangdong, Peoples R China
来源：
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY | 2023年 / 83卷
关键词：
Zn- Nb-Ti ternary system; Continuous solid solution; Experimental phase equilibria; 450-DEGREES-C ISOTHERMAL SECTION; THERMODYNAMIC ASSESSMENT; MICROSTRUCTURE; FORMABILITY;
D O I：
10.1016/j.calphad.2023.102630
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
In order to determine the isothermal sections of Zn-Nb-Ti ternary phase diagram at 600 and 450 degrees C, the equilibrated alloy method was adopted by using scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction. The experimental results show that there are seven and ten three-phase regions at the 600 and 450 degrees C isothermal sections, respectively. Besides, a continuous homogeneous solid solution (Nb,Ti)Zn3 phase was further identified, of which the lattice parameters increase with the increasing of Nb content in these two isothermal sections. Compared with the 450 degrees C isothermal section, the homogeneity range of (Nb,Ti)Zn3 phase increases slightly at 600 degrees C. No ternary compounds were detected at both 600 and 450 degrees C isothermal sections.
引用
收藏
页数：10
相关论文
共 50 条
  • [1] Phase equilibria of Zn-Al-Ti ternary system at 450 and 600 °C
    Wang, Wei
    Li, Zhi
    Shen, Wei-jun
    Yin, Fu-cheng
    Liu, Ya
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2020, 30 (04) : 1005 - 1016
  • [2] Experimental investigation of the phase equilibria of the La-Ti-Zn system at 600 and 450 °C
    Wu, Changjun
    Fan, Sailin
    Peng, Haoping
    Liu, Ya
    Wang, Jianhua
    Su, Xuping
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2018, 62 : 61 - 66
  • [3] Phase Equilibria of the Zn-Bi-Co System at 450 and 600 °C
    Huixin Liu
    Manxiu Zhao
    Fucheng Yin
    Yongxiong Liu
    Zhi Li
    Journal of Phase Equilibria and Diffusion, 2015, 36 : 535 - 543
  • [4] Phase equilibria of the Co-Cu-Zn system at 600 °C and 450 °C
    Liu, Yongxiong
    Zhao, Manxiu
    Li, Zhi
    Chen, Bihong
    Yin, Fucheng
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2018, 62 : 119 - 127
  • [5] Phase equilibria of the Co-Ni-Zn system at 450°C and 600°C
    Zhao, Manxiu
    Wang, Zhanhui
    Yin, Fucheng
    Li, Zhi
    Long, Zhaohui
    THERMOCHIMICA ACTA, 2012, 545 : 103 - 111
  • [6] Phase Equilibria of the Zn-Bi-Co System at 450 and 600 °C
    Liu, Huixin
    Zhao, Manxiu
    Yin, Fucheng
    Liu, Yongxiong
    Li, Zhi
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2015, 36 (06) : 535 - 543
  • [7] Ternary Phase Equilibria at 450 °C in the Zn-Fe-P System
    Zhi Li
    Xuping Su
    Yuehui He
    Journal of Phase Equilibria and Diffusion, 2008, 29 : 11 - 19
  • [8] Ternary phase equilibria at 450 °C in the Zn-Fe-P system
    Li, Zhi
    Su, Xuping
    He, Yuehui
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2008, 29 (01) : 11 - 19
  • [9] Phase Equilibria of the Al-Zn-Fe-Ti Quaternary System at 600 A°C
    Li, Zhi
    Shen, Weijun
    Yin, Fucheng
    Wang, Xinming
    Wu, Yu
    Zhao, Manxiu
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2013, 34 (03) : 211 - 220
  • [10] Phase Equilibria of the Al-Zn-Fe-Ti Quaternary System at 600 °C
    Zhi Li
    Weijun Shen
    Fucheng Yin
    Xinming Wang
    Yu Wu
    Manxiu Zhao
    Journal of Phase Equilibria and Diffusion, 2013, 34 : 211 - 220