Enhanced Cr(VI) Photocatalysis Reduction by Layered N-doped TiO2 Sheets from Template Free Solvothermal Method

被引：0
|
作者：
Zhang, Xinyi [1 ]
Yang, Jingxia [1 ]
Wang, Jinjie [1 ]
机构：
[1] Shanghai Univ Engn Sci, Coll Chem & Chem Engn, LongTeng Rd 333, Shanghai 201620, Peoples R China
来源：
CHEMCATCHEM | 2023年 / 15卷 / 22期
基金：
上海市自然科学基金;
关键词：
Cr(VI) removal; layered structure; N doping; photocatalysis; TiO2; SURFACE OXYGEN VACANCIES; TITANIUM-DIOXIDE; EFFICIENT PHOTOREDUCTION; CEO2; NANOFLAKES; WASTE-WATER; NANOPARTICLES; PERFORMANCE; DEGRADATION; NANOSHEETS; FABRICATION;
D O I：
10.1002/cctc.202301007
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Layered TiO2 sheets with high Cr(VI) photoreduction ability were prepared by template free solvothermal method using ethylene glycol (EG) as structure directing agent. EG linking function in the layered TiO2 structure were confirmed by SEM, TEM, FTIR, XPS and so on. Moreover, the obtained large sized TiO2 (20 similar to 50 mu m in length, about 5 similar to 10 mu m in width) were assembled by N-doped TiO2 thin sheets with about 1.2 nm gap in between, resulting in very high surface area (327.5 m(2)/g) and abundant Ti3+ sites for Cr(VI) adsorption and reduction. This structure can not only have good performance during Cr(VI) photocatalysis reduction application (Cr(VI) removal rate: 0.84 mg*g(-1)*min(-1)), but also endow the material with good cycle ability.
引用
收藏
页数：11
相关论文
共 50 条
  • [1] One-step solvothermal synthesis of N-doped TiO2 nanoparticles with high photocatalytic activity in the reduction of aqueous Cr(VI)
    Li, Jing
    Yang, Min
    Jiang, Zun-Biao
    [J]. CHINESE CHEMICAL LETTERS, 2014, 25 (02) : 283 - 286
  • [2] Enhanced photoactivity of N-doped TiO2 for Cr(VI) removal: Influencing factors and mechanism
    Wang, Shu Qin
    Liu, Wen Bo
    Fu, Peng
    Cheng, Wei Liang
    [J]. KOREAN JOURNAL OF CHEMICAL ENGINEERING, 2017, 34 (05) : 1584 - 1590
  • [3] Enhanced photoactivity of N-doped TiO2 for Cr(VI) removal: Influencing factors and mechanism
    Shu Qin Wang
    Wen Bo Liu
    Peng Fu
    Wei Liang Cheng
    [J]. Korean Journal of Chemical Engineering, 2017, 34 : 1584 - 1590
  • [4] Solvothermal synthesis of N-doped TiO2 nanotubes for visible-light-responsive photocatalysis
    Jiang, Zheng
    Yang, Fan
    Luo, Nianjun
    Chu, Bryan T. T.
    Sun, Deyin
    Shi, Huahong
    Xiao, Tiancun
    Edwards, Peter P.
    [J]. CHEMICAL COMMUNICATIONS, 2008, (47) : 6372 - 6374
  • [5] Preparation and Photocatalysis Property of N-Doped TiO2 Film
    Zhao Hongsheng
    Hu Hongpo
    Zhang Kaihong
    Li Ziqiang
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (10) : 1815 - 1817
  • [6] Synthesis of N-doped TiO2 mesosponge by solvothermal transformation of anodic TiO2 nanotubes and enhanced photoelectrochemical performance
    Wang, Qingyao
    Yang, Xiuchun
    Wang, Xuelai
    Huang, Min
    Hou, Junwei
    [J]. ELECTROCHIMICA ACTA, 2012, 62 : 158 - 162
  • [7] One-step solvothermal synthesis of N-doped TiO2 nanoparticles with high photocatalytic activity in the reduction of aqueous Cr(Ⅵ)
    Jing Li
    Min Yang
    Zun-Biao Jiang
    [J]. Chinese Chemical Letters, 2014, 25 (02) : 283 - 286
  • [8] Electrospinning synthesis of N-doped TiO2 fiber membranes and its enhanced photocatalysis performance
    Jie Gao
    Lingfan Zhang
    Junchao Qian
    Feng Chen
    Wenqing Zhang
    [J]. Chemical Papers, 2021, 75 : 115 - 122
  • [9] HNO3-involved one-step low temperature solvothermal synthesis of N-doped TiO2 nanocrystals for efficient photocatalytic reduction of Cr(VI) in water
    Zhang, Yong Cai
    Yang, Min
    Zhang, Geshan
    Dionysiou, Dionysios D.
    [J]. APPLIED CATALYSIS B-ENVIRONMENTAL, 2013, 142 : 249 - 258
  • [10] Brief Review on the preparation of N-doped TiO2 and Its Application to Photocatalysis
    Oh, Kyeongseok
    Hwang, Duck Kun
    [J]. KOREAN CHEMICAL ENGINEERING RESEARCH, 2019, 57 (03): : 331 - 337
12345