Preparation, Characterization, and Antibacterial Activity of Silver Nanoparticle-Decorated Ordered Mesoporous Carbon

In this study, Ordered Mesoporous Carbon (OMC) was prepared using resol as a carbon precursor and F127 as a soft template. Small-angle X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM) images, and nitrogen adsorption and desorption isotherms revealed that OMC possessed ordered hexagonal mesostructures (p6m) with an ordered pore size of 3.2nm, a high specific surface area (S-BET) of 539m(2) /g, and a large total pore volume (V-total) of 0.44cm(3) /g. Subsequently, silver nanoparticles synthesized from an aqueous AgNO3 solution using glucose as a reducing agent and starch as a stabilizing agent were decorated on OMC, producing Ag/OMC. XRD analysis revealed that the composite contained silver crystals. In addition, the content and size of silver nanoparticles in Ag/OMC were 0.71wt% (AAS) and around 25-50nm (TEM), respectively. Due to the surface cover of silver nanoparticles, S-BET and V-total of Ag/OMC slightly decreased to 417m(2)/g and 0.38cm(3)/g, respectively. Both agar and broth dilution techniques were used to evaluate the antibacterial activity of the material against Staphylococcus aureus. Ag/OMC with a Minimum Inhibitory Concentration (MIC) of 25.0 mu g/mL is a potential candidate for use against Staphylococcus aureus.