Area effect during the fracture process of high-Niobium-Titanium-Aluminum alloys under continuous tension loading-unloading

被引:0
|
作者
Zhong, Mingjie [1 ]
Lin, Youzhi [1 ,2 ]
机构
[1] Zhanjiang Univ Sci & Technol, Zhanjiang, Peoples R China
[2] Texas A&M Univ, Artie McFerrin Dept Chem Engn, College Stn, TX 77843 USA
关键词
high-Niobium-Titanium-Aluminum alloys; tension loading-unloading; area effect; fracture stress; damage mechanism; HIGH-NB; MECHANICAL-PROPERTIES; MICROSTRUCTURE EVOLUTION; TIAL ALLOYS; BEHAVIOR; TOUGHNESS;
D O I
10.3389/fmats.2023.1214873
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Based on the extracted results of the continuous tension loading-unloading testing, and observations of the corresponding cracks and fracture surfaces for the high-Niobium-Titanium-Aluminum alloys, both tensile damage and fracture mechanism were systematically studied. From the acquired results, it was demonstrated that the continuous tension loading-unloading did not affect the elastic modulus of the alloy. However, it decreased in fracture stress, fracture strain, and fracture work per unit area, and increased in irreversible strain. This result shows that the irreversible strain is not mainly caused by the volume effect of microcracks, but by the plastic strain of the materials. Although the density of the micro-cracks produced by multi-loading and unloading was small, most of the micro-cracks were concentrated on a certain section area, which results in an obvious area effect caused by the damage of the microcrack. In addition, the further propagation of the main crack under lower re-loading stress was not caused by the application of higher normal stress but by the residual tensile stress, which depends on the deterioration of the material at the crack tip during the unloading process of the alloy. These small amounts of microcracks are usually concentrated on the cross-sectional area, and the area effect caused by the microcracks damage is also obvious, which leads to a reduction of the fracture performance. Therefore, the area effect ultimately induces a decrease in fracture stress.
引用
收藏
页数:9
相关论文
共 11 条
  • [1] Phase transition of sulfur during continuous impact loading-unloading process
    Yang, Lei
    Liu, Qi-Jun
    Yang, Xue
    Liu, Fu-Sheng
    JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 2023, 181
  • [2] Seepage law of rough fracture during loading-unloading process considering 3D topography characteristics
    Sun Ke-ming
    Xin Li-wei
    Zhai Cheng
    Zhang Shu-cui
    Li Tian-shu
    ROCK AND SOIL MECHANICS, 2016, 37 (37) : 161 - 166
  • [3] Characteristics of damage and fracture process of carbon fiber reinforced plastic under loading-unloading test by using AE method
    Yeungnam Univ, Kyongsan, Korea, Republic of
    Mater Sci Eng A Struct Mater Prop Microstruct Process, (322-326):
  • [4] Characteristics of damage and fracture process of carbon fiber reinforced plastic under loading-unloading test by using AE method
    Kim, ST
    Lee, YT
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 234 : 322 - 326
  • [5] Fracture of aircraft titanium alloys under high-frequency loading
    Nikitin, Alexander D.
    Shesterkin, Pavel S.
    Lopatin, Sergey S.
    SN APPLIED SCIENCES, 2023, 5 (02):
  • [6] Fracture of aircraft titanium alloys under high-frequency loading
    Alexander D. Nikitin
    Pavel S. Shesterkin
    Sergey S. Lopatin
    SN Applied Sciences, 2023, 5
  • [7] Substructure Evolution and Mechanical Properties in Martensitic Stainless Steel During a High Cycle Number of Repetitive High Stress Loading-Unloading Process
    Wei, Yudao
    Liao, Hengcheng
    Lan, Zhenlin
    Ling, Hong
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2024, 55 (10): : 4212 - 4234
  • [8] Influence of constituent particles on fracture of aluminum alloys under high-triaxiality loading
    Daehli, Lars Edvard Blystad
    Olufsen, Sindre Nordmark
    Kristensen, Tore Andre
    Borvik, Tore
    Hopperstad, Odd Sture
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 864
  • [9] Inhomogeneity of the plastic flow of titanium alloys under the high-speed loading during the explosion welding process
    Pavlyukova, D. B.
    Bataev, I. A.
    Mali, V. I.
    Zhuravina, T. V.
    Makarova, E. B.
    Yartsev, P. S.
    OBRABOTKA METALLOV-METAL WORKING AND MATERIAL SCIENCE, 2011, (02): : 46 - 47
  • [10] FATIGUE STRENGTH AND FATIGUE FRACTURE PROCESS OF HIGH TENSION BOLTS OF BORON STEEL TESTED UNDER AXIAL CYCLIC LOADING.
    Suzuki, Hideto
    Ouyabu, Masaru
    Kunio, Takeshi
    Zairyo/Journal of the Society of Materials Science, Japan, 1987, 36 (408) : 980 - 985