Semi-solid Tensile Behavior and its Relationship with Hot Tearing Susceptibility of Mg-xCa Alloys

被引：0

作者：

Zhao, Hua ^{[1
,2
]}

Song, Jiangfeng ^{[1
,2
]}

Wang, Jing ^{[1
,2
]}

Liu, Qiang ^{[1
,2
]}

Chen, Gong ^{[1
,2
]}

Xiao, Jianfei ^{[1
,2
]}

Liao, Jin'ge ^{[1
,2
]}

Teng, Hang ^{[3
]}

Jiang, Bin ^{[1
,2
]}

Pan, Fusheng ^{[1
,2
]}

机构：

[1] Chongqing Univ, Natl Engn Res Ctr Magnesium Alloys, Chongqing 400045, Peoples R China

[2] Chongqing Univ, Natl Key Lab Adv Casting Technol, Chongqing 400044, Peoples R China

[3] Nanjing Yunhai Special Met Co Ltd, Nanjing 211212, Peoples R China

来源：

INTERNATIONAL JOURNAL OF METALCASTING | 2024年 / 18卷 / 02期

基金：

中国国家自然科学基金;

关键词：

magnesium alloy; Mg-Ca alloy; semi-solid tensile; linear contraction; hot tearing; MECHANICAL-PROPERTIES; MAGNESIUM ALLOY;

D O I：

10.1007/s40962-023-01097-4

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

To figure out the relationship between semi-solid deformation and hot tearing susceptibility of magnesium alloys, the solid and semi-solid tensile experiments of binary Mg-xCa (x = 0.2, 0.5, and 2 wt%) alloys were conducted by a Gleeble 3500 thermal simulator. The linear contraction of the alloys was measured by a newly developed apparatus based on a constrained rod casting (CRC) hot tearing apparatus. The results indicated that the ultimate tensile strength (UTS) and fracture elongation (FE) of the alloys decreased with the decrease in solid fraction (increase in the test temperature). It is revealed that Mg-0.5Ca alloy exhibited the highest hot tearing susceptibility due to its extremely low ductility even at a high solid fraction of 0.96 and the highest linear contraction among the three alloys.

引用

页码：1119 / 1134

页数：16

共 50 条

[1] Semi-solid Tensile Behavior and its Relationship with Hot Tearing Susceptibility of Mg–xCa Alloys
Hua Zhao
Jiangfeng Song
Jing Wang
Qiang Liu
Gong Chen
Jianfei Xiao
Jin’ge Liao
Hang Teng
Bin Jiang
Fusheng Pan
International Journal of Metalcasting, 2024, 18 : 1119 - 1134
[2] Reduction of Hot Tearing of Cast Semi-Solid 206 Alloys
Lemieux, Alain
Langlais, Joseph
Chen, X-Grant
SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES XII, 2013, 192-193 : 101 - +
[3] Mechanical properties in the semi-solid state and hot tearing of aluminium alloys
Eskin, DG
Suyitno
Katgerman, L
PROGRESS IN MATERIALS SCIENCE, 2004, 49 (05) : 629 - 711
[4] Effect of calcium on the microstructure and corrosion behavior of microarc oxidized Mg-xCa alloys
Pan, Yaokun
Chen, Chuanzhong
Feng, Rui
Cui, Hongwei
Gong, Benkui
Zheng, Tingting
Ji, Yarou
BIOINTERPHASES, 2018, 13 (01)
[5] Residual stresses of the as-cast Mg-xCa alloys with hot sprues by neutron diffraction
Song, Jiangfeng
Huang, Yuanding
Kainer, Karl Ulrich
Gan, Weimin
Hort, Norbert
RESIDUAL STRESSES IX, 2014, 996 : 592 - 597
[6] Hot tensile behavior of an extruded Al-Zn-Mg-Cu alloy in the solid and in the semi-solid state
Chen, Gang
Jiang, Jufu
Du, Zhiming
Han, Fei
Atkinson, H. V.
MATERIALS & DESIGN, 2014, 54 : 1 - 5
[7] A new methodology for measurement of semi-solid constitutive behavior and its application to examination of as-cast porosity and hot tearing in aluminum alloys
Phillion, A. B.
Cockcroft, S. L.
Lee, P. D.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2): : 237 - 247
[8] Meso-scale modelling of semi-solid deformation in aluminum foundry alloys: Effects of feeding and microstructure on hot tearing susceptibility
Sheykh-jaberi, F.
Cockcroft, S. L.
Maijer, D. M.
Phillion, A. B.
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2020, 279
[9] Hot tearing susceptibility and fluidity of semi-solid gravity cast Al-Cu alloy
Wannasin, J.
Schwam, D.
Yurko, J. A.
Rohloff, C.
Woycik, G.
SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES, 2006, 116-117 : 76 - 79
[10] Semi-solid processing of Al and Mg alloys
Shehata, MT
Zoqui, EJ
Kao, V
Essadiqi, E
Materials in the Automotive Industry, 2001, : 207 - 223

← 1 2 3 4 5 →