Nanoporous carbons based on coordinate organic polymers as an efficient and eco-friendly nano-sorbent for adsorption of phenol from wastewater

The major part of water pollutants includes of organic such as phenolic pollutant, thus there are every hazardous to environment. Present work is a comparative onto surface chemistry and adsorptive characteristics of coordinate organic polymer (Cop-150) and nanoporous carbon (NPC) prepared using solvothermal method. New NPC was successfully synthesized to remove of phenol. FT-IR, XRD, XPS, SEM, TGA, and BET techniques have been used to characterization and confirm physicochemical variation during preparing Cop-150 and NPC. Box-Behnken response surface methodology (BBRSM) was used to optimize four important factors of the pH (2-10), contact time (1-40 min), temperature (25-60 & DEG;C), and initial concentration of phenol (5-50 mg L-1). To analyze the data obtained from the adsorption of phenol by synthesized adsorbents, four linear, 2FI, quadratic and cubic models were examined, which the quadratic model was recognized as the best model. To the NPC the equal adsorption capacity 500 mg g(-1) is achieved at the initial concentration of phenol = 49.252 mg L-1, contact time = 15.738 min, temperature = 28.3 & DEG;C, and pH 7.042. On the other hand, the adsorption capacity for Cop-150 in pH 4.638, the contact time = 19.695 min, the temperature = 56.8 & DEG;C, and the initial concentration of phenol = 6.902 mg L-1 was equal to 50 mg g(-1). The experimental data at different conditions were investigated by some famous kinetic and isotherm models, which among them, were corresponded to the pseudo-second-order kinetic model and the Langmuir isotherm. Moreover, based to result of thermodynamics to the both Cop-150 and NPC, the adsorption process is exothermic and spontaneous. According to results the Cop-150 and NPC could be used for up to four and five cycles without significantly reducing their performance, respectively.