Preparation and corrosion resistance of polyaniline and waterborne polyurethane composite coating film

Polyaniline (PANI) particles were synthesized using aniline (AN), dodecyl benzene sulfonic acid (DBSA), and ammonium persulfate (APS). The particles were analyzed using scanning electron microscope (SEM), X-ray diffraction (XRD), and fourier transform infrared spectroscopy (FTIR). A PANI/waterborne polyurethane composite material (PANI-WPU) was obtained by combining it with polyethylene glycol (PEG600), diphenylmethane diisocyanate (MDI), dimethylol propionic acid (DMPA), N-methyl pyrrolidone (NMP), and dibutyltin lauric acid (DBTDL). The structure was characterized by the FTIR spectrum. The mechanical characteristics of the coating film were evaluated with respect to the PANI content, as well as its water absorption, glossiness, electrochemical corrosion resistance, and acid and alkali resistance. The PANI/waterborne polyurethane film has a maximum tensile strength of 23 +/- 1$$ \pm 1 $$ MPa, an elongation of 1012%, a pencil hardness of 5H, a flexibility of 2 mm, an impact resistance of 50 cm, the water absorption of 14.66%, and the glossiness of 99.9 +/- 0.1$$ \pm 0.1 $$ at 60 degrees. When the PANI content is 0.7%, the mechanical characteristics, glossiness, and anti-corrosion performance of the composite film improve. The corrosion inhibition efficiency of the aqueous polyurethane coating film with PANI can reach 99.74%, as shown by the examination of electrochemical polarization curves and impedance spectra. The tinplate is coated with a 0.7% PANI-WPU composite material and edge sealing. This coating provides excellent protection against acid and alkali resistance, as demonstrated by its ability to withstand immersion in 10% H2SO4 and 10% NaOH solution for 90 days without any paint peeling off.