Improved corrosion resistance of TiAlCrNbMo alloy to lead-bismuth eutectic by pre-oxidation

被引：2
|
作者：
Liu, Y. [1 ]
Ge, H. E. [2 ]
Ren, Q. S. [2 ]
Deng, H. W. [1 ]
Li, Z. [1 ]
Du, B. [1 ]
Zhang, T. [1 ]
机构：
[1] Guangzhou Univ, Res Ctr Adv Informat Mat CAIM, Sch Phys & Mat Sci, Guangzhou 510006, Guangdong, Peoples R China
[2] China Nucl Power Technol Res Inst, Shenzhen 518031, Guangdong, Peoples R China
来源：
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2024年 / 28卷
关键词：
LBE; TiAl alloy; Oxidation; Anti-corrosion; Nuclear materials; OXIDATION BEHAVIOR; LIQUID LEAD; THERMAL-EXPANSION; TEMPERATURE; STEELS; ANATASE; COMPATIBILITY; CHROMIUM; RUTILE; LBE;
D O I：
10.1016/j.jmrt.2023.12.044
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A Ti48.5Al46Cr3Nb0.5Mo2 alloy was designed and fabricated to investigate its corrosion resistance to static liquid lead-bismuth eutectic (LBE). The microstructure and corrosion behavior of un-oxidized and pre-oxidized samples were compared. The results show that LBE preferentially penetrated into the alloy along the CrMo-rich sigma phase formed at high-temperature. A TiO2 and Al2O3 oxide layer was formed on the surface of the matrix after 2 h pre-oxidized leading to remarkable LBE resistance. When extended the pre-oxidized time to 4 h, the exfoliation of the oxide layer caused by the evaporation of MoO3 significantly weakens the corrosion resistance.
引用
收藏
页码：707 / 718
页数：12
相关论文
共 50 条
  • [1] FeCrMoWCBY metallic glass with high corrosion resistance in molten lead-bismuth eutectic alloy
    Wei, X. S.
    Jin, J. L.
    Jiang, Z. Z.
    Liang, D. D.
    Shen, J.
    CORROSION SCIENCE, 2021, 190
  • [2] A novel FeCrAlWx high entropy alloy coating for enhancing lead-bismuth eutectic corrosion resistance
    Zhang, Peng
    Yao, Zhongping
    Wang, Xinzhi
    Zheng, Yang
    Cui, Kai
    Yao, Rui
    Lin, Shouyuan
    Liu, Yanyan
    Lu, Songtao
    Wu, Xiaohong
    JOURNAL OF NUCLEAR MATERIALS, 2024, 589
  • [3] Corrosion of ODS steels in lead-bismuth eutectic
    Hosemann, P.
    Thau, H. T.
    Johnson, A. L.
    Maloy, S. A.
    Li, N.
    JOURNAL OF NUCLEAR MATERIALS, 2008, 373 (1-3) : 246 - 253
  • [4] HEAT OF SOLIDIFICATION OF LEAD-BISMUTH EUTECTIC ALLOY
    TIWARI, SN
    SINGH, HP
    MALHOTRA, SL
    MISRA, S
    SCRIPTA METALLURGICA, 1971, 5 (10): : 895 - &
  • [5] A novel AlCrFeMoTi high-entropy alloy coating with a high corrosion-resistance in lead-bismuth eutectic alloy
    Yang, Jian
    Shi, Ke
    Zhang, Wei
    Chen, Qingsong
    Ning, Zhien
    Zhu, Changda
    Liao, Jiali
    Yang, Yuanyou
    Liu, Ning
    Zhang, Wei
    Yang, Jijun
    CORROSION SCIENCE, 2021, 187
  • [6] Corrosion of irradiated NbMoVCr coatings in lead-bismuth eutectic
    Yang, Jian
    Zhong, Yilong
    Long, Bin
    Li, Lu
    Qu, Guofeng
    Lu, Shenghui
    Yang, Jijun
    CORROSION SCIENCE, 2024, 237
  • [7] Critical temperature of the lead-bismuth eutectic (LBE) alloy
    Azad, AM
    JOURNAL OF NUCLEAR MATERIALS, 2005, 341 (01) : 45 - 52
  • [8] Impedance spectroscopy and microstructural characterization of the corrosion behavior of FeCrAl alloy in lead-bismuth eutectic
    Chen, Xiang
    Haasch, Rick
    Stubbins, James F.
    JOURNAL OF NUCLEAR MATERIALS, 2012, 431 (1-3) : 125 - 132
  • [9] Corrosion Behavior of Stainless Steel 410 in Flowing Lead-Bismuth Eutectic Alloy at 550℃
    Ju N.
    Lei Y.
    Chen G.
    Zhu Q.
    Li T.
    Wang D.
    Cailiao Daobao/Materials Reports, 2019, 33 (10): : 3489 - 3493
  • [10] The oxidation of alloy HT-9 during immersion in lead-bismuth eutectic and a method for measuring instantaneous corrosion rate
    Lillard, RS
    Valot, C
    Hanrahan, RJ
    SURFACE OXIDE FILMS, 2004, 2003 (25): : 259 - +
12345