Electrochemical corrosion behavior of atmospheric-plasma-sprayed copper as a coating material for deep geological disposal canisters

Cu, which exhibits excellent corrosion resistance in underground environments, has been investigated as a canister material for use in the deep geological disposal of spent nuclear fuels. In this study, the technical viability of atmospheric plasma spraying for producing Cu-coated canisters was investigated. A high-purity Cu film (millimeter scale) was deposited onto a stainless-steel substrate using a plasma gun with a shroud structure. Potentiodynamic polarization studies revealed that the Cu film exhibited a sufficiently low corrosion rate in the groundwater electrolyte. In addition, no pitting corrosion was observed on the Cu film surface after accelerated corrosion studies. A prototype cylindrical Cu film was fabricated on a 1/20 scale on a stainless-steel tube to demonstrate the scalability of atmospheric plasma spraying in producing Cu-coated canisters.