Enhanced electro-strain with high electrostrictive performances of Bi0.5Na0.4K0.1TiO3 based lead-free piezoelectric ceramics by Ba(Fe0.5Nb0.5) O3

Complex piezoelectric ceramics of (1-x)[0.97(Bi0.5Na0.4K0.1)TiO3-0.03(Ba0.7Sr0.3)TiO3]-xBa(Fe0.5Nb0.5)O3 or (1x)[0.97BNKT-0.03BST]-xBFN were investigated, where the x value was between 0 and 0.03. All compositions were synthesized via a conventional mixed oxide method. X-ray diffraction and Raman spectroscopy techniques indicated that all ceramics exhibited a coexistence of rhombohedral (R) and tetragonal (T) phases without any impurity phase. However, the T phase became dominant at higher BFN contents. The maximum temperature (Tm), the ferroelectric to ergodic relaxor phase transition temperature (TF-R), and Burn's temperature (TB) decreased with increasing BFN content, while the dielectric constant at Tm was enhanced for the x = 0.01 ceramic. The BFN additive interrupted ferroelectric ordering, which led to constriction in the hysteresis loops as well as large electric field-induced strains (Smax = 0.42%), a normalized strain coefficient (d*33 = Smax/Emax = 846 pm/V), and an electrostrictive coefficient (Q33 = 0.0432 m4/C2) for the x = 0.01 ceramic under a moderate applied electric field of 50 kV/cm. These results indicated that this ceramic had the potential for electromechanical applications.