Effect of Temperature and Impurity Content to Control Corrosion of 316 Stainless Steel in Molten KCl-MgCl2 Salt

被引：10
|
作者：
Li, Na [1 ,2 ]
Wang, Huaiyou [3 ]
Yin, Huiqin [1 ]
Liu, Qi [1 ]
Tang, Zhongfeng [1 ,2 ,4 ]
机构：
[1] Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China
[2] Univ Chinese Acad Sci, Beijing 100049, Peoples R China
[3] Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China
[4] Dalian Natl Lab Clean Energy, Dalian 116023, Peoples R China
来源：
MATERIALS | 2023年 / 16卷 / 05期
基金：
国家重点研发计划; 中国国家自然科学基金;
关键词：
corrosion; high temperature; KCl-MgCl2; molten salt; alloy; THERMAL-ENERGY STORAGE; BEHAVIOR;
D O I：
10.3390/ma16052025
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The corrosion resistance of 316 stainless steel (316SS) in molten KCl-MgCl2 salts was studied through static immersion corrosion at high temperatures. Below 600 degrees C, the corrosion rate of 316SS increased slowly with increasing temperature. When the salt temperature rises to 700 degrees C, the corrosion rate of 316SS increases dramatically. The corrosion of 316SS is mainly due to the selective dissolution of Cr and Fe at high temperatures. The impurities in molten KCl-MgCl2 salts could accelerate the dissolution of Cr and Fe atoms in the grain boundary of 316SS, and purification treatment can reduce the corrosivity of KCl-MgCl2 salts. Under the experimental conditions, the diffusion rate of Cr/Fe in 316SS changed more with temperature than the reaction rate of salt impurities with Cr/Fe.
引用
收藏
页数：12
相关论文
共 50 条
  • [1] Effect of In-situ Self-Generated MgO on Corrosion Resistance of KCl-MgCl2 Molten Salt
    Yang Taisen
    Zhang Guiqing
    Dai Zhiyong
    Liang Xuewei
    Wang Yingdi
    Su Yunhai
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (05) : 1268 - 1276
  • [2] HOT corrosion behavior of inconel 625 cladding metal in KCl-MgCl2 molten salt
    Yang, Taisen
    Su, Yunhai
    Su, Ming
    Dai, Zhiyong
    Wang, YingDi
    Liang, Xuewei
    MATERIALS TODAY COMMUNICATIONS, 2024, 38
  • [3] Corrosion behaviour of 316 stainless steel in NaCl-KCl-MgCl2 salt vapour at 700°C
    Liu, Qi
    Xu, Hongxia
    Yin, Huiqin
    Li, Na
    Wang, Wenrui
    Li, Linfan
    Tang, Zhongfeng
    Qian, Yuan
    CORROSION SCIENCE, 2022, 194
  • [4] Effect of stainless steel on the corrosion of pressureless-sintered SiC in the vapor of molten NaCl-KCl-MgCl2 salt
    Wang, Xiaodong
    Yang, Xinmei
    Hu, Miaomiao
    Liu, Huajian
    Zhou, Xingtai
    CORROSION SCIENCE, 2022, 205
  • [5] Corrosion behavior of Inconel 625 deposited metal in molten KCl-MgCl2
    Yang, Taisen
    Su, Yunhai
    Liu, Hongyu
    Dai, Zhiyong
    Liang, Xuewei
    Wu, Xinggang
    MATERIALS RESEARCH EXPRESS, 2020, 7 (12)
  • [6] Intergranular corrosion of 316H stainless steel induced by SO42- ions in MgCl2-KCl-NaCl molten salt
    Ai, Hua
    Chen, Yanjun
    Yang, Xinmei
    Sun, Hua
    Su, Xingzhi
    Yan, Long
    Huang, Wei
    Gong, Yu
    SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2024, 271
  • [7] Corrosion of type 316L stainless steel in molten LiCl-KCl salt
    Shankar, A. Ravi
    Mudali, U. Kamachi
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2008, 59 (11): : 878 - 882
  • [8] Effect of excess Mg to control corrosion in molten MgCl2 and KCl eutectic salt mixture
    Hanson, Kasey
    Sankar, Krishna Moorthi
    Weck, Philippe F.
    Startt, Jacob K.
    Dingreville, Remi
    Deo, Chaitanya S.
    Sugar, Joshua D.
    Singh, Preet M.
    Corrosion Science, 2022, 194
  • [9] Effect of excess Mg to control corrosion in molten MgCl2 and KCl eutectic salt mixture
    Hanson, Kasey
    Sankar, Krishna Moorthi
    Weck, Philippe F.
    Startt, Jacob K.
    Dingreville, Remi
    Deo, Chaitanya S.
    Sugar, Joshua D.
    Singh, Preet M.
    CORROSION SCIENCE, 2022, 194
  • [10] High temperature corrosion behaviour of the 316 stainless steel in NaCl-KCl-AlCl3 molten salt and its vapour
    Chen, Saijun
    Liu, Qi
    Guo, Fangyuan
    Chen, Liuping
    Tang, Zhongfeng
    CORROSION SCIENCE, 2024, 227
12345