CaO-MgO-Al2O3-SiO2 (CMAS) corrosion behaviour of LaMgAl11O19/GdPO4 thermal barrier coating materials

被引：3

作者：

Song, Chenxi ^{[1
]}

Qi, Xiang ^{[1
]}

Huang, Ling ^{[1
]}

Sun, Junbin ^{[1
,2
,3
,4
]}

Li, Lizhen ^{[1
]}

Li, Chenguang ^{[1
]}

Lu, Weihong ^{[1
,2
,3
]}

机构：

[1] Hengyang Normal Univ, Coll Chem & Mat Sci, Hengyang 421008, Peoples R China

[2] Hengyang Normal Univ, Hunan Prov Key Lab Funct Met Organ Cpds, Hengyang 421008, Peoples R China

[3] Hengyang Normal Univ, Coll Hunan Prov, Key Lab Organomet New Mat, Hengyang 421008, Peoples R China

[4] Hengyang Normal Univ, Hunan Engn Res Ctr Monitoring & Treatment Heavy Me, Hengyang 421008, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2023年 / 49卷 / 16期

基金：

中国国家自然科学基金;

关键词：

CMAS corrosion; GdPO4; MAGNESIUM-ALUMINA-SILICATE; CONDUCTIVITY; CERAMICS; TEMPERATURE; RESISTANCE; LA; GD; SM; ND;

D O I：

10.1016/j.ceramint.2023.05.193

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

CaO-MgO-Al2O3-SiO2 (CMAS) corrosion poses serious hidden dangers for the application of thermal barrier coatings (TBCs). In this study, LaMgAl11O19 (LMA) and GdPO4 were mixed at molar ratios of 2:1, 1:1 and 1:2 to prepare LMA/GdPO4 materials, and the CMAS corrosion behaviours of these materials were investigated at 1300 & DEG;C-1500 & DEG;C for 20 h and 40 h. It was demonstrated that temperature was the main factor influencing the corrosion behaviours and products. The materials were damaged at 1300 & DEG;C by the crystallization of CMAS melts to form CaAl2Si2O8. In contrast, the materials were corroded by CMAS melts via the reaction between CMAS and GdPO4 at 1500 & DEG;C. These results indicate that the addition of GdPO4 to LMA can improve the resistance of the LMA material to CMAS corrosion.

引用

页码：26578 / 26588

页数：11

共 50 条

[1] Corrosion Behavior of CMAS on LaMgAl11O19 Coating
Wang Yajun
Ma Xinxin
Ma Rui
Tang Guangze
Liu Ling
RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (08) : 2927 - 2932
[2] In situ synthesis of α-alumina layer on thermal barrier coating for protection against CMAS (CaO-MgO-Al2O3-SiO2) corrosion
Zhang, Xiao-feng
Zhou, Ke-song
Xu, Wei
Chen, Bo-yu
Song, Jin-bing
Liu, Min
SURFACE & COATINGS TECHNOLOGY, 2015, 261 : 54 - 59
[3] Research of in situ modified PS-PVD thermal barrier coating against CMAS (CaO-MgO-Al2O3-SiO2) corrosion
Song, Jinbing
Zhang, Xiaofeng
Deng, Chumming
Deng, Changguang
Liu, Min
Zhou, Kesong
Tong, Xin
CERAMICS INTERNATIONAL, 2016, 42 (02) : 3163 - 3169
[4] Thermochemical interaction of thermal barrier coatings with molten CaO-MgO-Al2O3-SiO2 (CMAS) deposits
Kramer, Stephan
Yang, James
Levi, Carlos G.
Johnson, Curtis A.
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2006, 89 (10) : 3167 - 3175
[5] CMAS corrosion behavior of LaMgAl11O19/CeO2 ceramic materials
Ou, Jiani
Bin, Xing
Liu, Zhihua
Sun, Junbin
Lu, Weihong
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2024, 44 (06) : 3747 - 3759
[6] Degradation characteristics of thermal barrier coatings for hot corrosion and CaO-MgO-Al2O3-SiO2
Park, Kwang-Yong
Jang, Kyung-Ic
Myoung, Sang-Won
Jung, Yeon-Gil
Yang, Byung-Il
Kim, Jun-Seong
SURFACE & COATINGS TECHNOLOGY, 2021, 412
[7] Degradation of Yttria Stabilized Zirconia Thermal Barrier Coatings by Molten CMAS (CaO-MgO-Al2O3-SiO2) Deposits
Mohan, Prabhakar
Yuan, Biao
Patterson, Travis
Desai, Vimal
Sohn, Yongho
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 207 - 212
[8] INDIRECT DISSOLUTION OF (AL,CR)2O3 IN CAO-MGO-AL2O3-SIO2 (CMAS) MELTS
SANDHAGE, KH
YUREK, GJ
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (08) : 1941 - 1954
[9] Nanostructured Gd2Zr2O7: a promising thermal barrier coating with high resistance to CaO-MgO-Al2O3-SiO2 corrosion
Bahamirian, M.
JOURNAL OF THE AUSTRALIAN CERAMIC SOCIETY, 2023, 59 (01) : 165 - 177
[10] Corrosion resistance of GdPO4 thermal barrier coating candidate in the presence of CMAS+NaVO3 and CMAS
Guo, Lei
Feng, Jiayi
Meng, Shijun
CORROSION SCIENCE, 2022, 208

← 1 2 3 4 5 →