Dendrite-free deposition and side-reaction suppression of zinc anodes achieved via constructing synergistic interface buffer layers

Aqueous zinc metal batteries (ZMBs) are expected to be used in grid-scale storage systems due to their superior intrinsic safety and the low manufacturing cost of zinc anodes. However, uncontrolled dendrite deposition and side-reaction pose challenges to the durable operation of ZMBs on a large scale. Herein, we construct a bifunctional buffer layer for zinc anodes (delta-MnO2@Zn), aiming to achieve dendrite-free deposition and side-reaction suppression of zinc anodes that are suitable for large-scale use. Density functional theory calculations and electric field simulations revealed that the delta-MnO2 coating facilitates the desolvation of Zn2+ and promotes uniform diffusion and deposition of Zn2+ on the Zn anode surface. In addition, the porous delta-MnO2 coating acts as a physical buffer layer, and can reduce rampant dendrite deposition by regulating the Zn2+ concentration field and reducing the local current density. Furthermore, the zincophilic delta-MnO2 coating acts as a chemical buffer layer, reducing the amount of bound water in the Zn2+ solvent shell and inhibiting unfavorable side-reaction of the Zn anode. As expected, the delta-MnO2@Zn symmetric cell demonstrates a lifespan of more than 1000 h at a rate of 0.5 mA cm(-2) with 0.25 mA h cm(-2). Moreover, the full battery assembled with a carbon-based cathode demonstrated outstanding cycling behavior of over 11 500 cycles at 2 A g(-1). The conclusions demonstrate the principle of a synergistic interfacial buffer layer on the Zn anode surface, guiding the development of advanced artificial interface layers.