Mechanical Properties of Fiber-Reinforced Permeable Geopolymer Concrete

In this paper, permeable geopolymer concrete with high compressive strength and permeability is prepared using alkali-activated metakaolin as a slurry, and its mechanical properties are reinforced by adding steel fibers. The influencing factors of the strength, porosity and permeability coefficient of the fiber-reinforced permeable geopolymer concrete, as well as its microstructure and curing mechanism, are determined by conducting an unconfined compressive strength test, scanning electron microscopy, energy-dispersive spectroscopy and X-ray diffraction. The test results show that, under the water permeability required to meet the specification conditions, when the alkali activator modulus is 1.4 and the activation-to-solid ratio is 0.9, the effect of metakaolin activation is the most obvious, and the unconfined compressive strength of the permeable geopolymer concrete is the highest. Moreover, the paste formed via the alkali activation of metakaolin contains a large number of silica-oxygen and aluminum-oxygen bonds with a dense and crack-free structure, which enables the paste to tightly combine with the aggregates; the strength of the permeable geopolymer concrete is early strength, and its strength at a curing age of 3 days is the highest. The strength at a curing age of 3 days can reach 43.62% of the 28-day strength; the admixture of steel fiber can effectively improve the strength of the permeable concrete, and with an increase in the amount of admixture, the strength of the fiber shows a trend of increasing, and then decreasing. Under the conditions of this test, a volume of steel fiber of 0.3% enables the optimum unconfined compressive strength to be reached.